具有优良耐化性和抗冲击性的化学强化玻璃制造技术

本发明专利技术提供了一种玻璃或化学强化玻璃，其包含或由以下组成：SiO2 69.8～72.2％；Al2O3 0.2～0.5％；Na2O 12.8～14.0％；K2O 0～0.25％；MgO 4.6～6.5％；CaO 8.0～10.0％；SrO 0～0.15％；BaO 0～0.15％；B2O3 0～0.5％；ZrO2 0～0.2％；其中，SiO2+∑RO的摩尔百分数之和大于等于84％，其中∑RO表示MgO、CaO、SrO和BaO的摩尔百分数之和。根据本发明专利技术的玻璃具有优良的耐化性和抗冲击性的化学强化玻璃。所述玻璃可以在电子显示设备、例如电视机中用作背板玻璃。

Has excellent chemical resistance and impact resistance of glass

The present invention provides a glass or toughened glass, comprising or consisting of the following: SiO2 69.8 ~ 72.2%; Al2O3 0.2 ~ 0.5%; Na2O 12.8 ~ 14%; K2O 0 ~ 0.25%; MgO 4.6 ~ 6.5%; CaO 8 ~ 10%; SrO 0 ~ 0.15%; BaO 0 0.15% ~ 0 ~ 0.5%; B2O3; ZrO2 0 ~ 0.2%; among them, SiO2+ RO and sigma mole percentage greater than or equal to 84%, the sigma RO representation and MgO, CaO, the mole fraction of SrO and BaO. Chemically strengthened glass with excellent chemical resistance and impact resistance according to the present invention. The glass can be used as a backing glass in an electronic display device, such as a TV set.

【技术实现步骤摘要】
具有优良耐化性和抗冲击性的化学强化玻璃
本专利技术一般地涉及玻璃，特别地涉及具有优良的耐化性和抗冲击性的化学强化玻璃。所述玻璃可以在电子显示设备、例如电视机、笔记本电脑、平板显示器或智能手机中用作背板玻璃。
技术介绍
通常，显示设备使用的背板以塑料件为主，其具有分量轻、易成型、适宜小屏幕等特点，曾一度占领着显示设备背板市场。但在户外或化工场所使用的显示设备，由于塑料件耐化性差，易被腐蚀老化，影响设备使用寿命。同时在另一方面，随着触控技术发展，特别是随着OGS技术发展，显示设备逐渐趋向于一体化，设备背板、显示器以及保护盖板构成一个整体。这就要求作为显示设备使用的背板，要与显示器及保护盖板具有较高的契合度，同时要具备耐化性，塑料件已无法满足要求。为了解决上述问题，本专利技术意在提供一种具有优良耐化性和抗冲击性的玻璃。该玻璃一方面可以解决塑料件耐化性差，影响设备使用寿命的问题，另一方面，作为与显示器及保护盖板同材质的玻璃，无论是在与显示器及保护盖板的粘合衔接方面，还是外观整体性方面，都将具有塑料件无法比拟的优势。
技术实现思路
本专利技术在第一方面中提供了一种玻璃，以氧化物基准的摩尔百分数表示本文档来自技高网...

【技术保护点】
一种玻璃，以氧化物基准的摩尔百分数表示，其包含或由以下组成：

【技术特征摘要】
1.一种玻璃，以氧化物基准的摩尔百分数表示，其包含或由以下组成：其中：SiO2+∑RO的摩尔百分数之和大于等于84％、优选大于等于85％，其中∑RO表示MgO、CaO、SrO和BaO的摩尔百分数之和。2.根据权利要求1所述的玻璃，其中，SiO2+∑RO的摩尔百分数之和小于等于87％，优选小于等于86％。3.根据权利要求1所述的玻璃，其中，Na2O+K2O的摩尔百分数之和小于等于14.2％，优选小于等于14％。4.根据权利要求1所述的玻璃，其为厚度在0.5mm至2mm之间的玻璃板。5.一种化学强化玻璃，其为权利要求1-4中任一项的玻璃经化学强化处理而得到的化学强化玻璃。6.根据权利要求5的化学强化玻璃，其中，根据...

【专利技术属性】
技术研发人员：刘再进，宫汝华，陈佳佳，何根，
申请(专利权)人：四川旭虹光电科技有限公司，
类型：发明
国别省市：四川,51