活性炭的制备方法及活性炭技术
Preparation method of activated carbon and activated carbon
Carbon preparation and activity of the present invention relates to an activated carbon. A preparation method of activated carbon, in a protective gas atmosphere, the straw carbonization of carbide in the 300 to 400 DEG C; the carbides and alkali mixed uniformly to obtain mixture, the quality of the carbide and alkali ratio of 1:3 to 1:4; the protective gas atmosphere, the mixture at 500 to 800 DEG C for 1 hours to 2 hours activation treatment and pre product; the product pre impregnated in inorganic acid, at 80 - 90 DEG C for 1 hours to 2 hours by activated carbon. The activated carbon prepared by the method of activated carbon can increase the specific capacity of the supercapacitor.
【技术实现步骤摘要】
活性炭的制备方法及活性炭
本专利技术涉及一种活性炭的制备方法及活性炭。
技术介绍
随着经济的发展和生活水平的提高，能源问题和环境污染问题日益严重，新型无污染能源的开发和应用是各国科研人员正在研究的热点问题。超级电容器以充放电时间短、循环寿命长、使用温度范围宽、兼具物理电容器的高比功率和电池的高比能量的优异特性迅速吸引了人们的注意。超级电容器又称电化学电容器或双电层电容器，已在电动汽车、移动通讯、太阳能和风力发电、航空航天和国防科技等方面发挥着重要作用。电极材料作为超级电容器的重要组成部分，在超级电容器充放电过程中，电极材料的孔结构以及比表面积的大小都会影响测试过程中电解液离子的脱嵌，故电极材料在很大程度上影响着超级电容器的性能，并直接决定着其成本的高低。因此，可以通过提高电极材料的性能来提高超级电容器的电化学性能，并通过降低电极材料的生产成本来降低超级电容器的成本。碳材料由于具有制备简便、比表面积大、导电性好、孔径可控以及成本低廉等优点使其引起了研究者广泛的兴趣，而研究较多的碳材料主要有活性炭、碳纤维和碳纳米管等，其中活性炭是最早也是最多被用于超级电容器的材料。目...
【技术保护点】
一种活性炭的制备方法，其特征在于，包括以下步骤：在保护性气体氛围下，将秸秆在300℃～400℃下进行碳化得到碳化物；将所述碳化物与强碱混合均匀得到混合物，所述碳化物与强碱的质量比为1：3～1：4；在保护性气体氛围下，将所述混合物在500℃～800℃下进行活化处理1小时～2小时得到预产物；及将所述预产物浸渍在无机强酸中，在80℃～90℃下保温1小时～2小时得到活性炭。
【技术特征摘要】
1.一种活性炭的制备方法，其特征在于，包括以下步骤：在保护性气体氛围下，将秸秆在300℃～400℃下进行碳化得到碳化物；将所述碳化物与强碱混合均匀得到混合物，所述碳化物与强碱的质量比为1：3～1：4；在保护性气体氛围下，将所述混合物在500℃～800℃下进行活化处理1小时～2小时得到预产物；及将所述预产物浸渍在无机强酸中，在80℃～90℃下保温1小时～2小时得到活性炭。2.根据权利要求1所述的活性炭的制备方法，其特征在于，所述秸秆为玉米秸秆。3.根据权利要求1所述的活性炭的制备方法，其特征在于，所述将秸秆在300℃～400℃下进行碳化得到碳化物的步骤中，所述碳化的时间为2小时～4小时。4.根据权利要求1所述的活性炭的制备方法，其特征在于，所述将所述碳化物与强碱混合均匀得到混合物的步骤中，...
【专利技术属性】
技术研发人员：于开锋，朱贺，曹兴刚，王中书，邹康迪，
申请(专利权)人：吉林大学，深圳市朗能电池有限公司，
类型：发明
国别省市：吉林,22