本发明专利技术属于冶金球团烧结技术领域，具体涉及一种球团生产的干燥预热新方法。本发明专利技术改变了现有的链篦机鼓干段气流进入方式，采取至料层上方抽风的方式，使链篦机鼓干段物料下层产生形成2000‑3000Pa负压，利用除尘风机使环冷机3冷段热风通过链篦机鼓干段，采用270℃‑300℃热风对生球预热，预计链篦机鼓干段烟罩温度为80℃‑100℃，能够满足生球预热温度，同时降低链篦机机尾周围环境温度，提高上托轴轴承使用寿命，取消了鼓干段放扇，对废弃粉尘进行回收利用。

A new method of drying preheating for pellet production

The present invention belongs to the field of metallurgy pellet sintering technology, and concretely relates to a new drying preheating method for pellet production. The invention changes the grate drum existing dry air into the way to take the material layer above the ventilation mode, the grate drum dry material produced 2000 3000Pa lower negative pressure, using the dust blower to cooler cooling section 3 hot air through the grate drum drying stage, using 270 C 300 C hot air ball preheating, is expected to grate drum dry hood temperature of 80 DEG C 100, can satisfy the pellet preheating temperature, while reducing the grate tail ambient temperature, improve the service life of the bearing on the supporting shaft, cancel the stem section of drum fan, dust for recycling of waste.

【技术实现步骤摘要】
一种球团生产的干燥预热新方法
本专利技术属于冶金球团烧结
，具体涉及一种球团生产的干燥预热新方法。
技术介绍
目前，国内现有链篦机回转窑制备球团工艺普遍使用的预热方式为三室四段式，即鼓风干燥段-抽风干燥段-预热一段-预热二段。其中我国球团厂鼓风干燥段均采用鼓干风机预热的方式，即通过鼓干风机将环冷机三冷段热风送入链篦机鼓干段，环冷机3冷段热风通过鼓干风机从鼓干段下部进入，对生球进行预热，如说明书附图图1所示，热风从料层下部进入，链篦机鼓干段正压，正压产生热风从链篦机鼓干段侧密封溢出，热气长期烘烤上托轴轴承座，缩短轴承使用寿命，同时预热后废气直接从链篦机鼓干段放扇外排到空气中，废弃粉尘造成设备周围环境污染，不利于热风中精矿粉的回收再利用。专利技术目的针对现有技术存在的问题，本专利技术提供一种球团生产的干燥预热新方法，目的是通过改变鼓干段压力，节约能源，提高除尘灰回收率，降低生产成本。本专利技术的球团生产的干燥预热新方法按照以下步骤进行：在链篦机鼓干段的料层上部，从链篦机两侧入孔门进行管道接引，使用除尘风机抽风，使料层下部热风入口处形成2000-3000Pa负压，将环冷机3冷段的60本文档来自技高网...

【技术保护点】
一种球团生产的干燥预热新方法，其特征在于按照以下步骤进行：在链篦机鼓干段的料层上部，从链篦机两侧入孔门进行管道接引，使用除尘风机抽风，使料层下部热风入口处形成2000‑3000Pa负压，将环冷机3冷段的600℃‑800℃热风引入鼓干段，形成独立热风循环系统，采用270℃‑300℃热风对生球团预热。

【技术特征摘要】
1.一种球团生产的干燥预热新方法，其特征在于按照以下步骤进行：在链篦机鼓干段的料层上部，从链篦机两侧入孔门进行管道接引，使用除尘风机抽风，使料层下部热风入口处形成2000-3000Pa负压，将环冷机3冷段的600℃-800℃热风引入鼓干段，形成独立热风循环系统，采用2...