The present invention relates to the technical field of surface treatment with the door frame, in particular to a door frame with surface treatment agent, wherein the door frame carrying by ammonium bifluoride, surfactant, potassium dichromate, chromium oxide, sodium phosphate, sulfuric acid, boric acid and water according to the weight ratio of 4 ~ 4.5:40 ~ 60:20 ~ 26:2 ~ 2.5:70 ~ 90:0.4 ~ 0.6:900 ~ 1200. The invention overcomes the defects of the existing technology, the processing agent is composed of ammonium bifluoride, potassium dichromate, chromium oxide, sodium phosphate, sulfuric acid, boric acid, water, only need to be processed with the door frame impregnation completed processing in processing agent for a certain period of time can be simple, easy to use, and the sources of raw materials, simple processing agent easy, low preparation cost, suitable for promotion.
【技术实现步骤摘要】
一种携门架表面处理剂
本专利技术涉及携门架表面处理
，具体属于一种携门架表面处理剂。
技术介绍
目前，现有的电动双开塞拉门的携门架包括连接板一、连接板二以及方管臂，该方管臂采用两个方管焊接而成，因此其工艺复杂，成本高，同时效率低下，而且采用焊接，其焊缝有气孔，融合差，因此方管臂的强度不高，结构性能差。在车门关闭时，车门容易发生偏移，导致车门关闭不严或者关闭错门，因此其密封、隔音效果差。同时其关闭不严、关闭错门，存在安全隐患，易造成安全事故。其中，焊接引起的焊缝区组织和性能的变化，会导致残余应力以及由此而导致的应力腐蚀裂纹，同时焊接位置和其他位置后续均需要进行打磨，打磨后需要进行表面处理，从而保证其防腐、防锈能力；但是现有的金属表面处理工序比较繁琐，耗时耗力。
技术实现思路
本专利技术的目的是提供了一种携门架表面处理剂，克服了现有技术的不足，处理剂由氟化氢铵、重铬酸钾、氧化铬、磷酸钠、浓硫酸、硼酸、水组成，只需要将加工完毕的携门架浸渍在处理剂一定时间即可完成处理，操作简单，使用方便，同时处理剂原料来源简单、易得，配制成本低，适合推广。为解决上述问题，本专利技术所采...
【技术保护点】
一种携门架表面处理剂，其特征在于，所述的携门架表面处理剂由氟化氢铵、重铬酸钾、氧化铬、磷酸钠、浓硫酸、硼酸、水按照重量比4～4.5：40～60：20～26 ：2～2.5：70～90：0.4～0.6：900～1200组成。
【技术特征摘要】
1.一种携门架表面处理剂，其特征在于，所述的携门架表面处理剂由氟化氢铵、重铬酸钾、氧化铬、磷酸钠、浓硫酸、硼酸、水按照重量比4～4.5：40～60：20～26：2～2.5：70～90：0.4～0.6：900～1200组成。2.根据权利要求1所述的一种携门架表面处理剂，其特征在于：所述的携门架表面处理剂由氟化氢铵、重铬酸钾、氧化铬、磷酸钠、浓硫酸、硼酸、水按照重量比4.2：50：22：2.2：80：0.5...
【专利技术属性】
技术研发人员：薛忠坤，杜永，
申请(专利权)人：合肥市瀚坤机械有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。