The invention relates to a super wear-resistant alloy material, which is characterized in that the super wear-resistant alloy material consists of 10 aluminum 25 tin, 1 5 copies, 5 copies of 1 rare earth, Mn 0.5 0.9 copies, 10 copies of the 6 vanadium, nickel 0.4 1.5. The technical scheme between the various components through the ingenious ratio, to meet the special requirements of the industry, the abrasion resistance of products is greatly improved; the technical scheme of wear resistant alloy has good abrasion resistance, excellent mechanical properties can meet the requirements of Engineering excavator, loader bucket tooth wear, pipeline, hammer crusher and jaw plate, various track in other parts of high strength, low cost and easy application further.
【技术实现步骤摘要】
超强耐磨合金材料
本专利技术涉及一种材料,具体涉及一种超强耐磨合金材料,属于合金材料
技术介绍
磨损是许多工业部门普遍存在并成为引起设备失效或材料破坏的一个重要原因,同时其也消耗了大量的能源和材料。由耐磨合金铸钢制造的各种工程挖掘机和装载机斗齿、各种耐磨输送管道、各种破碎机锤头和颚板、各种履带板,由于处于高强度、恶劣气候等工作条件,其磨损情况更加严重。合金,是由两种或两种以上的金属与金属或非金属经一定方法所合成的具有金属特性的物质。一般通过熔合成均匀液体和凝固而得。根据组成元素的数目,可分为二元合金、三元合金和多元合金。由于合金的性质,合金被广泛的应用在各个领域,随着应用的广泛,对合金的性质也有了更高的要求,但是目前市场上的合金耐磨性能、任性较差等,因此,迫切的需要一种新的方案解决该技术问题。
技术实现思路
本专利技术正是针对现有技术中存在的技术问题,提供一种超强耐磨合金材料,该技术方案满足特殊行业的要求,具有更高的耐磨性能,并且成本较低。为了实现上述目的,本专利技术的技术方案如下,一种超强耐磨合金材料,其特征在于,所述超强耐磨合金材料由以下成份组成:铝10-25份,锡1-5份,稀土1-5份,锰0.5-0.9份,钒6-10份,镍0.4-1.5份。一种超强耐磨合金材料,所述超强耐磨合金材料由以下成份组成:铝10份,锡1份,稀土1份,锰0.5份,钒6份,镍0.6份。一种超强耐磨合金材料,所述超强耐磨合金材料由以下成份组成:铝25份,锡5份,稀土5份,锰0.9份,钒10份,镍1.4份。一种超强耐磨合金材料,所述超强耐磨合金材料由以下成份组成:铝18份,锡2 ...
【技术保护点】
一种超强耐磨合金材料,其特征在于,所述超强耐磨合金材料由以下成份组成:铝10‑25份,锡1‑5份,稀土1‑5份,锰0.5‑0.9份,钒6‑10份,镍0.4‑1.5份。
【技术特征摘要】
1.一种超强耐磨合金材料,其特征在于,所述超强耐磨合金材料由以下成份组成:铝10-25份,锡1-5份,稀土1-5份,锰0.5-0.9份,钒6-10份,镍0.4-1.5份。2.根据权利要求1所述的超强耐磨合金材料,其特征在于,所述超强耐磨合金材料由以下成份组成:铝10份,锡1份,稀土1份,锰0.5份,钒6份,镍0.6份。3.根据权利要求1所述的超强耐磨合金材料,其特征在于,所述超强耐磨...