One kind of automobile parts coating and die casting method, which is in accordance with the following quality copies: 40 to 50 portions of phenol resin, dispersing agent 6 to 10 parts, high water retaining resin polyvinyl alcohol 15 - 20, 10 - 20, cobalt naphthenate defoaming agent 1 ~ 2 copies, 100 copies of deionized water, casting method auto parts coating, which in turn contains the following steps: (1) the raw material melt and heated to 800 to 900 DEG C, standing for 4 hours; (2) aligning parts, by roll coating, coating, vacuum spraying coating way for automobile parts, at the same time, after the hot air machine enhancement method of the wind; the invention provides a coating having simple preparation, convenient use, the effect of the treatment of spraying paint on the surface of automobile parts is improved, improve the protective effect of coating on the parts, convenient use, convenient to be used according to the needs, suitable for a variety of conditions of use.
【技术实现步骤摘要】
一种汽车零件涂料及其压铸方法
本专利技术属于汽车零件
，具体涉及一种汽车零件涂料及其压铸方法。
技术介绍
目前，涂料的使用与界面关系密切，涂料是一种多组分体系——树脂(基料)、颜填料、溶剂、助剂。在体系内部存在很多界面，特别是颜填料和树脂、溶剂之间存在一定界面；同时涂料是一种半成品，必须涂覆在工件、产品、结构上，才能提供保护、装饰、功能等作用，必然会存在一定界面状态，也为涂料使用提出了一定要求。此外，在涂料经施工后，有一个干燥、固化的过程，其中必然要考虑到涂膜表面和空气之间的表面，以保证能提供良好的涂膜外观，防止表面缺陷的出现。
技术实现思路
本专利技术要解决的技术问题是提供一种汽车零件涂料及其压铸方法，能快速生产出汽车零件表面处理涂料，改善涂料使用效果。为实现上述技术目的，达到上述技术效果，本专利技术通过以下技术方案实现：一种汽车零件涂料，按照如下质量份数组成：苯酚树脂40～50份、分散剂6～10份、高保水性树脂聚乙烯醇15～20份、环烷酸钴10～20份、消泡剂1～2份、去离子水100份。优选的，可以按照如下质量份数组成：苯酚树脂40份、分散剂6份、高保水性树...
【技术保护点】
一种汽车零件涂料，其特征在于：按照如下质量份数组成：苯酚树脂40～50份、分散剂6～10份、高保水性树脂聚乙烯醇15～20份、环烷酸钴10～20份、消泡剂1～2份、去离子水100份。
【技术特征摘要】
1.一种汽车零件涂料，其特征在于：按照如下质量份数组成：苯酚树脂40～50份、分散剂6～10份、高保水性树脂聚乙烯醇15～20份、环烷酸钴10～20份、消泡剂1～2份、去离子水100份。2.根据权利要求1所述的汽车零件涂料，其特征在于：按照如下质量份数组成：苯酚树脂40份、分散剂6份、高保水性树脂聚乙烯醇15份、环烷酸钴10份、消泡剂1份、去离子水100份。3.根据权利要求1所述的汽车零件涂料，其特征在于：按照如下质量份数组成：苯酚树...
【专利技术属性】
技术研发人员：项龙，张李华，查贵安，
申请(专利权)人：安徽瑞泰汽车零部件有限责任公司，
类型：发明
国别省市：安徽,34