The invention discloses a high concentration of graphene dispersion liquid and a preparation method thereof, belonging to the technical field of graphene dispersion system, which is based on the existing system of the dispersion of graphene added graphene aerogel as anti settling agent, graphite, graphene aerogel, dispersing agent, solvent proportion said after mixing the premix, mixed liquid, and the mixture of high shear mechanical stripping, can be prepared with high concentration of graphene concentration up to 70mg/ml dispersion, greatly improving the stability and dispersion of Shi Moxi improves the dispersion concentration, solve the dispersion problem of stratified precipitation, expansion the applications of graphene dispersions.
【技术实现步骤摘要】
一种高浓度石墨烯分散液及其制备方法
本专利技术涉及石墨烯分散体系
，具体涉及一种高浓度石墨烯分散液及其制备方法。
技术介绍
自2010年石墨烯获得诺贝尔奖以来，石墨烯本身具有的高导电性、高导热性引起广泛关注，并在储能、环境领域表现出优异的特性。但由于石墨烯层与层之间存在范德华力，易于团聚。在实际应用中，石墨烯材料需要分散在水及各种溶剂中，但是石墨烯材料大量团聚，从而使其很难分散于各种溶剂中，即使能够分散，由于石墨烯的纳米效应，也很难在高浓度下长时间稳定存在，大大限制了其应用。目前制备石墨烯分散液的方法主要有两种，一是采用氧化还原法获得石墨烯，再通过后期石墨烯改性，或加入表面活性剂获得石墨烯分散液；二是采用液相剥离，直接由石墨获得石墨烯分散液。第一种方法由于采用氧化还原法，反应中引入其它溶剂，不仅会造成合成石墨烯的缺陷多，同时反应中残存的溶剂对后续应用也存在负面影响，导致其性能下降，尤其是导电性，因此该方法获得的石墨烯分散液在其应用上受到极大限制。而第二种方法通过液相剥离法得到的石墨烯分散液，其石墨烯结构完整，品质质量高。但该方法产率低，石墨烯之间缺乏良好的界...
【技术保护点】
一种高浓度石墨烯分散液，其特征在于，包括如下组分及其重量份数：石墨1‑7份，防沉剂0.01‑0.1份，分散剂0‑0.4份，余量为溶剂，所述防沉剂采用石墨烯气凝胶。
【技术特征摘要】
1.一种高浓度石墨烯分散液，其特征在于，包括如下组分及其重量份数：石墨1-7份，防沉剂0.01-0.1份，分散剂0-0.4份，余量为溶剂，所述防沉剂采用石墨烯气凝胶。2.根据权利要求1所述的高浓度石墨烯分散液，其特征在于，所述石墨烯气凝胶的堆密度为0.001-0.01g/cm3，孔隙率89%-99%，吸油量300-600g/g，电导率＞1300S/m，比表面积＞1500m2/g。3.根据权利要求1所述的高浓度石墨烯分散液，其特征在于，所述分散剂采用CMC、PVP、聚乙二醇、CTAB、SBS、壳聚糖、羟甲基纤维素、海藻酸钠中的一种或两种以上组合。4.根据权利要求1所述的高浓度石墨烯分散液，其特征在于，所述溶剂采用水、甲醇、乙醇、N-甲基-2-吡咯烷酮、N,N-二甲基甲酰胺、四氢呋喃、二甲苯、丙酮、氯仿中的一种或两种以上组合。5.一种如权利要求1-4所述的高浓度石...
【专利技术属性】
技术研发人员：宋肖肖，郑逸群，苏阳，刘同浩，
申请(专利权)人：济宁利特纳米技术有限责任公司，
类型：发明
国别省市：山东,37