一种二维铋烯的制备方法及锂离子电池技术
Preparation method of two-dimensional Bi ene and lithium ion battery
The invention belongs to the field of new energy technology, and discloses a method for preparing a two-dimensional graphene bismuth, the method comprises the following steps: (1) the bismuth powder adding stripping solvent in ultrasonic vibration time, to obtain the mixed solvent; (2) the removal of the centrifugal mixed stripping solvent in bismuth powder. In order to obtain supernatant; (3) the centrifugal vacuum will get the supernatant high speed drying to obtain two-dimensional graphene bismuth. The present invention also relates to an electrode composition comprising a two-dimensional lithium ion battery. The two dimensional bismuth powder has high volume specific capacity and good circulation performance, and is stable, environmental friendly and pollution-free, and the preparation process is simple.
【技术实现步骤摘要】
一种二维铋烯的制备方法及锂离子电池
本专利技术属于新能源相关
，更具体地，涉及一种二维铋烯的制备方法及锂离子电池。
技术介绍
能源对于人类社会发展至关重要，但目前世界每年大部分的能源消耗是化石燃料，带来的温室效应和环境污染严重威胁我们的可持续发展。改变现有能源结构，大力发展风能、太阳能等清洁能源，能有效缓解这些问题。但是这些清洁能源本身固有的随机性、间歇性等缺点，导致难以满足便携式电子设备使用要求，比如太阳能只有在有光的情况下才能顺利发电，但是在晚上或者光线不好情况下很难获取能量，发展让我们随时随地都能用上能源的储能技术至关紧要。现阶段主流的储能技术包括物理类储能和电化学储能两大类，电化学储能技术具有效率高、投资少、使用安全、应用灵活等优点，非常适合当今能源的发展方向。锂离子电池具有重量轻、容量大、无记忆效应等优点，尤其手机、笔记本电脑等便携式电子设备在社会生活中的普及和大规模使用，大大促进了锂离子电池等电化学储能的开发和使用。但是，锂离子电池虽然能量密度很高，真正使用的负极材料石墨的理论体积容量只有837mAh/cm3，这限制了更小体积的便携式储能设备的发...
【技术保护点】
一种二维铋烯的制备方法，其特征在于，该方法包括下步骤：(1)将铋粉加入剥离溶剂内超声振动预定时间，在超声振动过程中，所述铋粉在所述剥离溶剂的作用下部分被剥离成片状，以此得到带片状铋烯的混合溶剂；(2)离心去除所述混合溶剂中未剥离的铋粉，以取得上清液，所述上清液中保留有所述片状铋烯；(3)将得到的所述上清液进行离心真空干燥，以得到片状的二维铋烯。
【技术特征摘要】
1.一种二维铋烯的制备方法，其特征在于，该方法包括下步骤：(1)将铋粉加入剥离溶剂内超声振动预定时间，在超声振动过程中，所述铋粉在所述剥离溶剂的作用下部分被剥离成片状，以此得到带片状铋烯的混合溶剂；(2)离心去除所述混合溶剂中未剥离的铋粉，以取得上清液，所述上清液中保留有所述片状铋烯；(3)将得到的所述上清液进行离心真空干燥，以得到片状的二维铋烯。2.如权利要求1所述的二维铋烯的制备方法，其特征在于：所述剥离溶剂为酒精、异丙醇、N-甲基吡咯烷酮、水中的一种或者几种的组合。3.如权利要求2所述的二...