涂覆纳米陶瓷涂层的火电厂锅炉水冷壁制造技术
Water wall of boiler in thermal power plant coated with nano ceramic coating
The present invention provides coated nano ceramic coatings of thermal power plant boiler water wall, the technical scheme is as follows: using emery sand or equivalent hardness of water cooling wall for sand blasting surface texturing, removing the oxide layer and the attachment, roughness of Sa12.5 micron; using compressed air spraying nano ceramic material, the thickness of the coating is 0.2 0.25mm. The invention has the advantages that the design is reasonable and practical, the coking degree of the boiler is greatly reduced, the operation efficiency of the boiler is improved, the time and effort are saved, and the utility model is suitable for popularization and application.
【技术实现步骤摘要】
涂覆纳米陶瓷涂层的火电厂锅炉水冷壁
本专利技术涉及非晶合金涂层
，尤其是涂覆纳米陶瓷涂层的火电厂锅炉水冷壁。
技术介绍
锅炉水冷壁由多个厚度为7mm碳钢管焊接而成，连为一体，安装在锅炉四周各部位，将锅炉燃烧产生的热能传导给水，并将水由液体转变为高温水蒸气，然后水蒸气驱动蒸汽轮机发电。由于煤质不同，部分煤高温燃烧后会产生一些胶质物，这些胶质物积累到一定程度形成厚度不等的堆积物附着在水冷壁上面，产生热防护现象，影响锅炉发热效率，造成能源浪费。结焦物也会使得水冷壁导热不均匀，在管道内部局部产生高压蒸汽或者水冷壁管干烧现象，造成爆管，在烟道等管道内，结焦物堆积到一定厚度，管径变细变窄，影响烟尘排放、不得不停炉清理，否则就会产生更大事故。目前电厂大多采用和优质煤掺烧的办法，然后不定期用人工使用电钻、钎子等工具现场清理结焦物。
技术实现思路
本专利技术经多年实践提供最先进的技术，是把美国LMC公司的纳米陶瓷材料涂覆到水冷壁表面上，解决水冷壁结焦问题。纳米陶瓷材料是一种高分子涂层材料，无毒、不挥发。涂层固化后，在水冷壁等管壁外形成一层致密度极高的防护膜，和水冷壁紧密结合，表面光滑，能够有效降低结焦物聚集。由于涂层厚度较薄，不会影响热传导效率。通过高压空气吹送，把纳米陶瓷涂层涂覆在水冷壁表面，从而大大降低锅炉结焦程度，提高锅炉运行效率。本专利技术的目的是通过以下技术方案实现的：采用金刚砂或同等硬度砂石对水冷壁表面进行喷砂毛化处理，去除氧化层和附着物，粗糙度达到Sa12.5微米。用压缩空气喷涂纳米陶瓷材料，喷涂厚度为0.2-0.25mm。本专利技术的有益效果：本专利技术设...
【技术保护点】
涂覆纳米陶瓷涂层的火电厂锅炉水冷壁，其特征在于：采用金刚砂或同等硬度砂石对水冷壁表面进行喷砂毛化处理，去除氧化层和附着物，粗糙度达到Sa12.5微米。
【技术特征摘要】
1.涂覆纳米陶瓷涂层的火电厂锅炉水冷壁，其特征在于：采用金刚砂或同等硬度砂石对水冷壁表面进行喷砂毛化处理，去除氧化层和附着物，粗糙度达到Sa12...
【专利技术属性】
技术研发人员：邢佑印，李明春，侯艳荣，
申请(专利权)人：山东金泰非晶科技有限公司，
类型：发明
国别省市：山东,37