The invention discloses a method for preparing algae filter medium, which comprises the following steps: 250 400 by weight of the composite clay, 30 100 parts by weight of polyvinyl chloride, 50 100 parts by weight of silicon carbide, 200 ceramic polishing slag, 300 parts by weight of 100 200 weight parts of two oxygen titanium, 50 100 parts by weight of polyolefin nano composite material mixing, pressing in molding device, and then in the 260 80 sintering under 300 DEG C for 120 minutes, cooled to 35 DEG C to release, filter media. The experimental results show that the removal rate of filter media can reach 100%, and the water quality does not change with the filtration time.
【技术实现步骤摘要】
一种过滤除藻介质的制备方法
本专利技术涉及水处理
,具体涉及一种过滤除藻介质的制备方法。
技术介绍
水体富营养化是指水中氮、磷、钾等元素含量过度增多，导致蓝藻等藻类及浮游动物等水体微生物呈恶性暴发式生长，并进一步使水体质量急剧下降的污染现象。淡水水体富营养化现象发生时，水面往往呈现各种不同颜色，故又称之为“水华”。富营养化水体中出现最多的生物是蓝藻和其他微小藻类，特别是蓝藻纲的铜绿微囊藻、鱼腥藻、颤藻等，此外，甲藻、鞭毛藻、硅藻、珊藻也常常是过度繁殖的种类。大量有害藻体在水中堆积生长并死亡后，会产生有害藻毒素、降低水的氧容量、散发硫化氢等化合物，给水体带来异味，使得细菌大量繁殖、水生动植物死亡，甚至产生致癌物而危害水体安全。因此有效去除水中藻体是保障水质的重要手段之一。
技术实现思路
本专利技术解决的技术问题在于提供一种过滤除藻介质的制备方法，用于去除水中藻等藻类及浮游动物等水体微生物，去除率较高。有鉴于此，本专利技术采取的具体技术方案是：一种过滤除藻介质的制备方法，包括以下步骤：将250-400重量份的复合粘土、30-100重量份的聚氯乙烯、50-100重量份...
【技术保护点】
一种过滤除藻介质的制备方法，其特征在于包括以下步骤：将250‑400重量份的复合粘土、30‑100重量份的聚氯乙烯、50‑100重量份的碳化硅、200‑300重量份的陶瓷抛光渣、100‑200重量份的二氧化钛、50‑100重量份的聚烯烃纳米复合材料混合，置于模压器中压制，然后在260‑300℃下烧结80‑120分钟，冷却至35℃脱模，得过滤介质；所述复合粘土是木节粘土、铁矾土和紫砂泥按照重量比3:2:1的比例混合制成；所述聚烯烃纳米复合材料包括以下组分：半结晶聚烯烃树脂和层状硅酸盐的纳米尺寸填料。
【技术特征摘要】
1.一种过滤除藻介质的制备方法，其特征在于包括以下步骤：将250-400重量份的复合粘土、30-100重量份的聚氯乙烯、50-100重量份的碳化硅、200-300重量份的陶瓷抛光渣、100-200重量份的二氧化钛、50-100重量份的聚烯烃纳米复合材料混合，置于模压器中压制，然后在260-300℃下烧结80-120分钟，冷却至35℃脱模，得过滤介质；所述复合粘土是木节粘土、铁矾土和紫砂泥按照重量比3:2:1的比例混合制成；所述聚烯烃纳米复合材料包括以下组分：半结晶聚烯烃树脂和层状硅酸盐的纳米尺寸填料。2.根据权利要求1所述的过滤除藻介质的制备方法，其特征在于烧结温度为280℃，烧结时间为100分钟。3.根据权利要求1所述...