一种改性香蕉茎杆生物质炭的制备方法技术
Preparation method of modified banana stalk biomass carbon
The invention discloses a preparation method of modified banana stalk biomass carbon. The banana stems were pressed and dried at 60 ~80, and they were crushed and screened. According to the solid-liquid ratio of banana stem powder and magnesium chloride solution 1:10~15g/ml, adding MgCl2 solution, shaking for 1 hours, dipping for 23 hours, filtering. Dry the filter residue in the oven. Then the product in the muffle furnace temperature is 400 DEG ~450 DEG in lean oxygen carbonization for 3.5 hours, and furnace cooling to room temperature, the product of grinding, 100 mesh sieve, which prepared the modified banana stem biomass carbon. The invention has simple technique, low production cost, NH4 N, PO4
【技术实现步骤摘要】
一种改性香蕉茎杆生物质炭的制备方法
本专利技术属于废物资源化利用和水污染处理
，具体涉及一种改性香蕉茎杆生物质炭的制备方法。
技术介绍
目前，全世界磷资源已严重短缺，同时规模化农业和工业生产又导致大量的氮、磷等元素排入地表水体中，造成水环境的富营养化。通过从污水和动物粪便中进行磷的回收不仅可以吸附水体氮磷,起到净化水质的作用，又实现了氮的回收和磷的利用，解决了我国复合缓释肥料缺乏等问题，其环境效益和社会效益十分显著。其中通过吸附剂回收废水中的氮、磷元素，由于其具有不产生二次污染，可再生回收等优点而备受重视。目前，最常用的吸附剂有活性碳和改性纤维素等，但是大多吸附剂因成本高或是生产工艺复杂而限制其应用。一些研究人员为降低成本采用了农业废弃物制备生物质碳进行氮磷的吸附。如采用甘蔗渣、花生壳、竹子、玉米渣、大豆秸秆、橡木、芦苇等不同原料制备的生物质炭处理初始浓度为5.0mg/l的KH2PO4溶液，发现花生壳对磷的吸附效果最好，但单位吸附量也只有3.8mg/g。香蕉属于热带水果，起源于亚洲东南部，是国际性大宗水果，具有生长周期短和产量高等特点，每年收获大量香蕉产品的...
【技术保护点】
一种改性香蕉茎杆生物质炭的制备方法，其特征在于具体步骤为：(1)将香蕉果实串中间的香蕉茎秆通过榨汁机，榨除香蕉茎秆的内部水分，再将得到的香蕉茎杆渣置于烘箱中，在60~80℃下烘干，最后用万能破碎机破碎后过60目筛，制得香蕉茎秆粉；(2)将步骤(1)制得的香蕉茎秆粉置于锥形瓶中，按香蕉茎秆粉与氯化镁水溶液固液比为1:10~15g/mL加入浓度为1.0~1.2mol/L的氯化镁水溶液，将锥形瓶加盖密封后进行振荡，振荡频率为150r/min，温度为30℃，振荡时间为1小时，然后再密封浸渍23小时，过滤，所得滤渣在105℃的烘箱中烘干，制得氯化镁改性香蕉茎秆粉；(3)将步骤(2)制...
【技术特征摘要】
1.一种改性香蕉茎杆生物质炭的制备方法，其特征在于具体步骤为：(1)将香蕉果实串中间的香蕉茎秆通过榨汁机，榨除香蕉茎秆的内部水分，再将得到的香蕉茎杆渣置于烘箱中，在60~80℃下烘干，最后用万能破碎机破碎后过60目筛，制得香蕉茎秆粉；(2)将步骤(1)制得的香蕉茎秆粉置于锥形瓶中，按香蕉茎秆粉与氯化镁水溶液固液比为1:10~15g/mL加入浓度为1.0~1.2mol/L的氯化镁水溶液，将锥形瓶加盖密封后进行振荡...
【专利技术属性】
技术研发人员：蒋艳红，朱义年，朱宗强，吴雨晴，叶成慧，林慕雨丹，
申请(专利权)人：桂林理工大学，
类型：发明
国别省市：广西,45