The present invention belongs to the field of refractory material technology, and mainly relates to a light heat insulating material containing silica micropowder. Light heat insulation material containing silicon oxide powder. It is composed of solid materials and liquid materials; the total mass percentage of solid raw material is 100%, the specific composition is: silica powder 1~85%; fumed silica 0~80%; refractory fiber 5~25%; foaming agent 2~20% acid; 0.1~10%; liquid raw materials for silica sol and water. Liquid raw materials accounted for 40~300% of the total solid material; wherein the silica sol is industrial silica sol, silica content was 28~30%. The invention achieves the purpose of controlling the thermal conductivity of the material and prolongs the service life of the equipment.
【技术实现步骤摘要】
一种含氧化硅微粉的轻质隔热材料
本专利技术属于耐火材料
，主要涉及一种含氧化硅微粉的轻质隔热材料。
技术介绍
轻质隔热材料由于其气孔率高、体积密度小、具有绝热性能，被普遍应用于各种工业窑炉内部耐火砖与钢壳之间的保温隔热衬体，获得良好的节能效果和高的能源利用率。常用的轻质隔热材料的体积密度为0.5～1.5g/cm3，对于体积密度小于0.5g/cm3的超轻质隔热材料，适合采用以下几种方法制造：1）填充物烧失法，将一些可燃物或易挥发物填充于料浆之中，利用高温下烧失掉填充物的方法，使材料具备多孔性。优点是：孔径尺寸和气孔率易控制。缺点是：强度偏低，气孔分布不均，且制作过程中会污染环境。2）多孔材料法，利用本身中空的材料为骨料，制作轻质隔热材料。优点是：颗粒孔径均匀，大小易于控制。缺点是：高温强度偏低，用在浇注料中材料易于分层，收缩线变化大；用在耐火砖中需要二次烧成，成本高，且不利于搬运。3）溶胶-凝胶法，把一些活性较高的化学物质均匀的混合到泥浆中，使之在泥浆中形成溶胶，通过缩聚反应，形成网络空间结构，最后干燥即可。优点是：孔径分布均匀，且多为微米以下的气孔，易于控制...
【技术保护点】
一种含氧化硅微粉的轻质隔热材料，其特征在于：所述的轻质隔热材料由固态原料和液态原料组成；固态原料的质量百分比总量为100%，具体组成如下：氧化硅微粉 1~85%；气相白炭黑 0~80%；耐火纤维 5~25%；发泡剂 2~20% ；酸 0.1 ~10%；液态原料为硅溶胶和水，所述的液态原料占固态原料总量的40~300%；其中硅溶胶为工业级硅溶胶，氧化硅的含量为28~30%。
【技术特征摘要】
1.一种含氧化硅微粉的轻质隔热材料，其特征在于：所述的轻质隔热材料由固态原料和液态原料组成；固态原料的质量百分比总量为100%，具体组成如下：氧化硅微粉1~85%；气相白炭黑0~80%；耐火纤维5~25%；发泡剂2~20%；酸0.1~10%；液态原料为硅溶胶和水，所述的液态原料占固态原料总量的40~300%；其中硅溶胶为工业级硅溶胶，氧化硅的含量为28~30%。2.根据权利要求1所述的一种含氧化硅微粉的轻质隔热材料，其特征在于：所述的气相白炭...
【专利技术属性】
技术研发人员：肖家志，张三华，梁亚丽，
申请(专利权)人：中钢集团洛阳耐火材料研究院有限公司，
类型：发明
国别省市：河南,41
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。