本发明专利技术涉及一种外墙保温板材及其制备方法，所述外墙保温板材由以下重量份的原料组成：粉煤灰20～40份；煤渣10～12份；水泥5～15份；生石灰2～8份；石膏8～16份；尾矿砂10～20份；钢渣6～8份；镍铁渣粉2～8份；粘结剂1～2份；阻燃剂2～3份。本发明专利技术的优点在于：本发明专利技术外墙保温板材的防火、抗压抗折强度高且保温隔热性能好。

External wall thermal insulation board

The present invention relates to an external wall insulation board and preparation method thereof, wherein the external wall insulation board is composed of the following parts by weight of the raw materials of fly ash from 20 to 40; 10 to 12 portions of cement cinder; 5 to 15; 2 to 8 portions of lime gypsum; 8 to 16; 10 to 20 portions of tailings from 6 to 8; steel slag; nickel slag powder of 2 to 8; 1 to 2 portions of binder; flame retardant agent 2 ~ 3. The present invention has the advantages of high fireproof, compressive and flexural strength and good heat insulation performance of the exterior wall insulation board.

【技术实现步骤摘要】
一种外墙保温板材
本专利技术属于建筑材料领域，特别涉及一种外墙保温板材。
技术介绍
建筑节能是我国节能工作的重要环节，用于建筑外墙外保温材料品种繁多，有无机材料、有机材料、复合材料等；用于梁、柱、剪力墙及非保温砌筑材料墙体作保温处理的均为板材或砂浆类保温材料。目前，建筑工程有采用外模内置硬泡聚氨酯板及外模内置模塑聚苯板现浇砼外墙外保温系统进行梁、柱及剪力墙部分外墙外保温施工，板材须采用耐碱网格布或钢丝网架加强，加工工艺复杂，造价昂贵。施工时须将板材与砼内钢筋连接固定，施工工艺复杂，且在20～25年使用年限后，这种系统一是造成污染、二是无法二次施工。针对上述情况，现大多采用A级防火保温材料进行施工，但目前市场上的A级防火保温板抗压强度不高、质地脆，作模板内置在浇筋砼捣振时极易破碎。
技术实现思路
本专利技术要解决的技术问题是提供一种防火、抗压抗折强度高且保温隔热性能好的外墙保温板材。为解决上述技术问题，本专利技术的技术方案为：一种外墙保温板材，其创新点在于：所述外墙保温板材由以下重量份的原料组成：粉煤灰20～40份；煤渣10～12份；水泥5～15份；生石灰2～8份；石膏8～16份；尾矿砂1本文档来自技高网...

【技术保护点】
一种外墙保温板材，其特征在于：所述外墙保温板材由以下重量份的原料组成：粉煤灰 20～40份；煤渣 10～12份；水泥 5～15份；生石灰 2～8份；石膏 8～16份；尾矿砂 10～20份；钢渣6～8份；镍铁渣粉 2～8份；粘结剂 1～2份；阻燃剂 2～3份。

【技术特征摘要】
1.一种外墙保温板材，其特征在于：所述外墙保温板材由以下重量份的原料组成：粉煤灰20～40份；煤渣10～12份；水泥5～15份；生石灰2～8份；石膏8～16份；尾矿砂10～...