一种可将玻璃棒拉加热制成玻璃丝的方法和装置制造方法及图纸

本发明专利技术涉及一种可将玻璃棒拉加热制成玻璃丝的方法和装置，所制备的玻璃丝可满足玻璃软化点、退火点及应变点温度测量使用。它是将玻璃棒固定在夹棒装置上，通过柔性细线与送棒装置相联，送棒装置速度可调，将玻璃棒送入由智能控温仪表控制的加热炉内，可调速的牵引机构上安装石墨制的主动轮与张紧轮，将玻璃棒加热拉伸制成玻璃丝，确保玻璃丝圆度和均匀性。

Method and device for making glass wire by pulling and heating glass rod

The invention relates to a method and a device for making glass wires by pulling and heating glass rods, and the prepared glass wires can meet the glass softening point, the annealing point and the temperature measurement of the strain point. It is a glass rod is fixed on the clamping rod device, through a flexible wire and rod feeding device which, feeding rod device speed adjustable glass rod into a heating furnace intelligent temperature control instrument control, traction mechanism speed of driving wheel mounted graphite and tensioner, glass rod heating and drawing made of glass fiber, glass fiber to ensure roundness and uniformity.

【技术实现步骤摘要】
一种可将玻璃棒拉加热制成玻璃丝的方法和装置
本专利技术涉及一种将玻璃棒加热拉制成玻璃丝的方法和装置，所制备的玻璃丝可满足玻璃软化点、退火点及应变点温度测量使用。
技术介绍
玻璃是一种非晶态材料，在受热过程中其性能表现出连续渐变特性，随着温度升高玻璃粘度逐步下降，其物质状态从刚性体转变成塑性体，进而呈现液体流动特性。玻璃热成型是从玻璃熔体流动状态快速冷却定型为固体状态，在玻璃熔体的冷却过程中，导致玻璃内部质点偏移平衡位置，产生显著的热应力，必须对玻璃材料进行退火处理来消除热应力，因此玻璃材料的应变点温度和退火点温度对于玻璃生产至关重要。总之，玻璃黏度对玻璃制造和加工过程起着决定性作用，在玻璃加工制造过程中，因此必须严格参照玻璃的温度-黏度特性曲线，才能保障玻璃的生产制造质量，尤其对于光学玻璃、电子玻璃的应力消除成为关键。玻璃黏度测量一般在高温区采用同轴旋转测量法(ASTMC-965MeasuringViscosityofGlassAbovetheSofteningPoint；ISO7884-2Determinationofviscositybyrotationviscometers)，本文档来自技高网...

【技术保护点】
一种可将玻璃棒加热拉制成玻璃丝的装置，其特征在于，夹棒装置下端用于夹持固定玻璃棒，夹棒装置上端与柔性线相联，柔性线绕过定滑轮固定在棘轮机构上，棘轮机构依靠送棒调速电机提供动力实现转动；热电偶用于测量加热炉炉膛内温度，控温箱上的智能控温仪表控制加热炉温度，加热炉的下方设置有牵引调速电机，牵引调速电机带动主动轮转动，张紧轮将玻璃丝压紧在主动轮上。

【技术特征摘要】
1.一种可将玻璃棒加热拉制成玻璃丝的装置，其特征在于，夹棒装置下端用于夹持固定玻璃棒，夹棒装置上端与柔性线相联，柔性线绕过定滑轮固定在棘轮机构上，棘轮机构依靠送棒调速电机提供动力实现转动；热电偶用于测量加热炉炉膛内温度，控温箱上的智能控温仪表控制加热炉温度，加热炉的下方设置有牵引调速电机，牵引调速电机带动主动轮转动，张紧轮将玻璃丝压紧在主动轮上。2.应用如权利要求1所述装置的方法，其特征在于：控温箱上的智能控温仪表控制加热炉升温到设定温度，玻璃棒加热拉制形成玻璃丝后，被牵引出加热炉；牵引调速电机带动主动轮...