The invention provides a paper plastic composite packaging materials, which are arranged by the upper surface of the polyethylene layer, printing ink layer and a base plate layer and a polyethylene layer, aluminum foil and Polyethylene double layer, which made the double polyethylene layer consists of the following raw materials by weight: Polyethylene 30, 10 2 guar gum 5 copies, 1.5 copies, 0.8 microcrystalline cellulose bentonite 0.4 1.5 copies, 0.5 copies, 0.2 TiO2 polycarbonate 1 3 copies, 3 copies, 1 lecithin crosslinked potato starch 1 3 and 0.8 chitosan 1.5. The packaging material of the invention has excellent resistance to breaking and withstanding voltage, and the resistance test shows that the test does not break at the height of 10m to the cement ground once, and the pressure resistance test shows that when the static pressure is 20MPa, the leakage is not leaked for 24 hours.
【技术实现步骤摘要】
一种纸铝塑复合软包装材料
本专利技术属于包装材料
，具体涉及一种纸铝塑复合软包装材料。
技术介绍
随着经济的高速发展和生活水平的不断提高，人们对包装材料健康和安全越来越重视，越来越多的人和企业投入到对包装材料的研究中。由于各种包装材料性能大不一样，单独的某一种或一层包装材料很难达到产品的要求，因此人们将两种或两种以上的包装材料用一定的复合方式制成复合包装。纸铝塑复合软包装就是在这种趋势下形成的一种包装形式。纸铝塑复合软包装材料以纸板、聚乙烯塑料和铝箔为主要基材，此外还含有少量油墨、涂料、胶黏剂等成分。目前，纸铝塑复合软包装多采用普通的聚乙烯，其保鲜期仅为3-6天，抗菌保鲜时间短，严重制约其作为乳制品包装的应用。
技术实现思路
解决的技术问题：本专利技术的目的是提供一种纸铝塑复合软包装材料。技术方案：一种纸铝塑复合软包装材料，由依次排列的表层聚乙烯层、印刷油墨层、原纸板层、聚乙烯层、铝箔和双聚乙烯层组成，其中，所述双聚乙烯层由以下按重量份计的原料制成：聚乙烯10-30份、瓜尔胶2-5份、微晶纤维素0.8-1.5份、膨润土0.4-1.5份、二氧化钛0.2-0.5份、...
【技术保护点】
一种纸铝塑复合软包装材料，其特征在于：由依次排列的表层聚乙烯层、印刷油墨层、原纸板层、聚乙烯层、铝箔和双聚乙烯层组成，其中，所述双聚乙烯层由以下按重量份计的原料制成：聚乙烯10‑30份、瓜尔胶2‑5份、微晶纤维素0.8‑1.5份、膨润土0.4‑1.5份、二氧化钛0.2‑0.5份、聚碳酸酯1‑3份、卵磷脂1‑3份、马铃薯交联淀粉1‑3份和壳聚糖0.8‑1.5份。
【技术特征摘要】
1.一种纸铝塑复合软包装材料，其特征在于：由依次排列的表层聚乙烯层、印刷油墨层、原纸板层、聚乙烯层、铝箔和双聚乙烯层组成，其中，所述双聚乙烯层由以下按重量份计的原料制成：聚乙烯10-30份、瓜尔胶2-5份、微晶纤维素0.8-1.5份、膨润土0.4-1.5份、二氧化钛0.2-0.5份、聚碳酸酯1-3份、卵磷脂1-3份、马铃薯交联淀粉1-3份和壳聚糖0.8-1.5份。2.根据权利要求1所述的纸铝塑复合软包装材料，其特征在于：所述表层聚乙烯层的厚度为80-100µm、印刷油墨层的厚度为10-20µm、原纸板层的厚度为50-100µm、聚乙烯层的厚度为10-30µm、铝箔的厚度为10-...
【专利技术属性】
技术研发人员：冯文田，冯超，
申请(专利权)人：句容市兴武包装有限公司，
类型：发明
国别省市：江苏,32