The invention discloses a varnish metal crafts, the raw materials consist of 70 parts: 50 epoxy resin; leveling agent: 2 5; phthalic anhydride two: 35 40; nano silica filler: 3 6; ethylene glycol: 25 30; nano negative ion powder: 1 3; has 15 copies: 10 acid; benzoguanamine resin: 150 190; butyl cellosolve: 3 8; p-toluenesulfonic acid: 1 2; the number of copies of all quality copies. Preferably, the epoxy resin is epoxy resin 1001. Preferably, the epoxy resin 1001 is 60 parts, and the portion number is the mass fraction. The beneficial effect of the invention is that the prepared varnish is evenly applied on the surface of the handicraft, and the utility model can effectively improve the erosion resistance of Arts and crafts, and can protect the handicraft articles for a long time.
【技术实现步骤摘要】
一种金属工艺品用清漆
本专利技术涉及一种金属工艺品用清漆。
技术介绍
清漆，又名凡立水，是由树脂为主要成膜物质再加上溶剂组成的涂料。由于涂料和涂膜都是透明的，因而也称透明涂料。涂在物体表面，干燥后形成光滑薄膜，显出物面原有的纹理。但清漆比普通漆更易受到环境污染的侵蚀，无法长时间保护工艺品。
技术实现思路
针对上述问题，本专利技术提供一种金属工艺品用清漆，提高工艺品抗侵蚀能力，可长时间保护工艺品。为实现上述技术目的，达到上述技术效果，本专利技术通过以下技术方案实现：一种金属工艺品用清漆，其原料组成为：环氧树脂：50-70份；流平剂：2-5份；邻苯二甲酸酐：35-40份；纳米二氧化硅填料：3-6份；乙二醇：25-30份；纳米负离子粉：1-3份；己二酸：10-15份；苯并胍胺树脂：150-190份；丁基溶纤剂：3-8份；对甲苯磺酸：1-2份；上述份数均为质量份数。优选，所述环氧树脂为环氧树脂1001。优选，所述环氧树脂1001为60份，份数为质量份数。优选，所述苯并胍胺树脂为175份，份数为质量份数。优选，所述邻苯二甲酸酐为36份，份数为质量份数。优选，所述乙二醇为28份，份数为质量份数。本专利技术的有益效果是：将制备的清漆均匀涂抹在工艺品表面，可有效提高工艺品抗侵蚀能力，可长时间保护工艺品。具体实施方式下面结合具体的实施例对本专利技术技术方案作进一步的详细描述，以使本领域的技术人员可以更好的理解本专利技术并能予以实施，但所举实施例不作为对本专利技术的限定。一种金属工艺品用清漆，其原料组成为：环氧树脂：50-70份；流平剂：2-5份；邻苯二甲酸酐：35-40份；纳米...
【技术保护点】
一种金属工艺品用清漆，其特征在于，其原料组成为：环氧树脂：50‑70份；流平剂：2‑5份；邻苯二甲酸酐：35‑40份；纳米二氧化硅填料：3‑6份；乙二醇：25‑30份；纳米负离子粉：1‑3份；己二酸：10‑15份；苯并胍胺树脂：150‑190份；丁基溶纤剂：3‑8份；对甲苯磺酸：1‑2份；上述份数均为质量份数。
【技术特征摘要】
1.一种金属工艺品用清漆，其特征在于，其原料组成为：环氧树脂：50-70份；流平剂：2-5份；邻苯二甲酸酐：35-40份；纳米二氧化硅填料：3-6份；乙二醇：25-30份；纳米负离子粉：1-3份；己二酸：10-15份；苯并胍胺树脂：150-190份；丁基溶纤剂：3-8份；对甲苯磺酸：1-2份；上述份数均为质量份数。2.根据权利要求1所述的一种金属工艺品用清漆，其特征在于，所述环氧树脂为环氧树脂100...