An aqueous silver paint of the invention, which is characterized by comprising the following raw materials in parts by weight: silver: 5 10; waterborne acrylic resin: 50 66; water soluble amino resin: 8 15; PVDF: 3 6; passivation 0.1: 1; defoaming agent: 0.01 1; anti settling agent: 0.2 5; solvent: 1 12; water: 10 22. An aqueous silver paint provided by the invention realizes the transformation of silver oily water, very stable after silver passivation treatment after water paint, not hydrolysis, flatulence, blackening, solve the aqueous silver metal and Baidu is not enough, with good adhesion to the substrate surface.
【技术实现步骤摘要】
一种水性银色烤漆
本专利技术涉及一种水性银色烤漆。
技术介绍
随着人们生活水平的提高,一些装潢设施所用的涂料除了要求具有基本的耐热性、耐磨性和耐候性等要求外,设计者往往追求给人以美观和闪亮的视觉效果。近年来,具有金属表面效果的粉末涂料也越来越多,然而,这些粉末涂料的金属表面效果往往不太稳定,容易随气压或静电压大小发生变化,附着效果不佳,因此,需要一种附着力好的银色水漆。
技术实现思路
为解决上述存在的问题,本专利技术的目的在于提供一种水性银色烤漆。所述水性银色烤漆实现了油性银粉水性化的转变,经处理钝化后的银粉在水性漆中很稳定,不会水解、胀气、发黑,解决了水性银粉金属感及百度不够的问题,对基材表面具有良好的附着力。为达到上述目的,本专利技术的技术方案是:一种水性银色烤漆,包括由如下重量份数的原料:银粉:5-10份;水性丙烯酸树脂:50-66份;水性氨基树脂:8-15份;聚偏氟乙烯:3-6份;钝化剂:0.1-1份;消泡剂:0.01-1份;防沉剂:0.2-5份;助溶剂:1-12份;水:10-22份。进一步地,包括由如下重量份数的原料:银粉:5-8份;水性丙烯酸树脂:50-60份;水性氨基树脂:8-11份;聚偏氟乙烯:3-4份;钝化剂:0.1-0.5份;消泡剂:0.01-0.1份;防沉剂:0.2-0.5份;助溶剂:4-10份;水:10-13份。进一步地,包括由如下重量份数的原料:银粉:6份;水性丙烯酸树脂:55份;水性氨基树脂:9份;聚偏氟乙烯:3.5份;钝化剂:0.4份;消泡剂:0.02份;防沉剂:0.3份;助溶剂:6.5份;水:11份。进一步地,所述消泡剂为有机硅 ...
【技术保护点】
一种水性银色烤漆,其特征在于,包括由如下重量份数的原料:银粉:5‑10份;水性丙烯酸树脂:50‑66份;水性氨基树脂:8‑15份;聚偏氟乙烯:3‑6份;钝化剂:0.1‑1份;消泡剂:0.01‑1份;防沉剂:0.2‑5份;助溶剂:1‑12份;水:10‑22份。
【技术特征摘要】
1.一种水性银色烤漆,其特征在于,包括由如下重量份数的原料:银粉:5-10份;水性丙烯酸树脂:50-66份;水性氨基树脂:8-15份;聚偏氟乙烯:3-6份;钝化剂:0.1-1份;消泡剂:0.01-1份;防沉剂:0.2-5份;助溶剂:1-12份;水:10-22份。2.根据权利要求1所述的一种水性银色烤漆,其特征在于,包括由如下重量份数的原料:银粉:5-8份;水性丙烯酸树脂:50-60份;水性氨基树脂:8-11份;聚偏氟乙烯:3-4份;钝化剂:0.1-0.5份;消泡剂:0.01-0.1份;防沉剂:0.2-0.5份;助溶剂:4-10份;水:10-13份。3.根据权利要求1所述的一种水性银...
【专利技术属性】
技术研发人员:陈小红,
申请(专利权)人:苏州日新水性涂料有限公司,
类型:发明
国别省市:江苏,32