一种用于风能发电的高延展性护套材料及其制备方法技术
High ductility sheath material for wind energy generation and preparation method thereof
The invention discloses a method for high ductility sheath material, wind power generation will include: straw ash and potassium feldspar powder were crushed, 200 mesh sieve, and both of them were at the temperature of 105 DEG C 120 mixer 6 8 minutes; the mixing the mixture of the two, into the torque rheological instrument, and then add the remaining residual material, and increase the temperature of 185 C 195 C 20 refining 25 minutes; the refining of colloids in three roll calender on a sheet, rubber roll cooling through the cooling output page, which is produced. The invention of sheath material with good elasticity, flexibility, elongation and tensile strength is high, and the burning flame retardant, low smoke, no harmful gas, suitable for long-term use of environmental exposure.
【技术实现步骤摘要】
一种用于风能发电的高延展性护套材料及其制备方法
本专利技术涉及风力发电
，特别是一种用于风能发电的高延展性护套材料及其制备方法。
技术介绍
作为新能源中技术最成熟的、最具规模开发条件和商业化发展前景的发电方式，风力发电的发展速度令人瞩目。作为风力发电设备配套产品的风力发电机用电缆正在成为有巨大市场潜力的电缆新品种。欧洲是风力发电的发源地，德国、荷兰等国的风电专用低温柔性电缆一般采用普通的橡胶绝缘和护套，而产品的主要标准有欧洲标准与德国标准，使用温度在-25-90℃，需要通过-25℃下3000次正反1080°低温抗扭转实验。我国的环境复杂多样，特别是风力资源发达的地区主要分布在西北高寒与东部沿海地区。西北高寒地区冬季的最低气温一般在-25℃以下，甚至有的地区达到-40℃，如内蒙古草原与青藏高原，东部沿海地区夏季的最高温度可能超过40℃，这些对于风能电缆都是严酷的挑战。为了保证风力发电设施的正常工作，我国的风能电缆在耐低温、耐扭转性能和耐盐浴性能上有着相对于传统风能电缆更高的要求。
技术实现思路
本专利技术的目的在于克服现有技术的不足，提供一种用于风能发电的高延展性...
【技术保护点】
一种用于风能发电的高延展性护套材料，其特征在于，由以下重量份的原料组成：秸秆灰10‑15份；钾长石粉1‑3份；聚磷酸铵3‑8份；PVC树脂粉20‑30份；氯磺化聚乙烯20‑30份；氧化镁3‑13份；二硫代氨基甲酸盐类1‑5份；氧化锌1‑4份；二苯胺0.5‑3份；N‑苯基‑2‑萘胺1‑3份；磷酸三苯酯3‑8份；三聚氰胺5‑6份；氯化石蜡8‑18份；补强剂20‑40份；钛酸酯偶联剂0.5‑2份。
【技术特征摘要】
1.一种用于风能发电的高延展性护套材料，其特征在于，由以下重量份的原料组成：秸秆灰10-15份；钾长石粉1-3份；聚磷酸铵3-8份；PVC树脂粉20-30份；氯磺化聚乙烯20-30份；氧化镁3-13份；二硫代氨基甲酸盐类1-5份；氧化锌1-4份；二苯胺0.5-3份；N-苯基-2-萘胺1-3份；磷酸三苯酯3-8份；三聚氰胺5-6份；氯化石蜡8-18份；补强剂20-40份；钛酸酯偶联剂0.5-2份。2.根据权利要求1所述一种用于风能发电的高延展性...
【专利技术属性】
技术研发人员：高举洪，
申请(专利权)人：成都巴吉科技有限公司，
类型：发明
国别省市：四川,51