本发明专利技术公开了一种PVC材料专用高遮盖环保易刮油墨，是由下述质量分数的材料制备而成的：铝基银浆20~25%、1/8秒硝化棉树脂10~15%、无毒增塑剂1~5%、煅烧高岭土5~10%、乙酯25~30%、异丙醇25~30%。本发明专利技术制备方法简单，只需将配方重量的原料混合均匀即可制备得到适合PVC基材的高遮盖环保易刮油墨，该油墨具有存储稳定、环保无毒害的特点。

PVC material dedicated high cover, environmental protection easy to scratch ink

The invention discloses a PVC material for high covering environmental protection easy scraping ink, is composed of the mass fraction of the material prepared by: aluminum silver paste 20~25%, 1/8 second nitrocellulose resin 10~15%, non-toxic plasticizer 1~5%, 5~10%, 25~30%, calcined kaolin ethyl isopropanol 25~30%. The preparation method of the invention is simple, and the high coverage environmental protection easy scratching ink suitable for the PVC base material can be prepared by mixing the ingredients of the formula weight uniformly, and the ink has the advantages of stable storage, environmental protection and no poison.

【技术实现步骤摘要】

本专利技术涉及油墨
，特别是涉及一种PVC材料专用高遮盖环保易刮油墨。
技术介绍
聚氯乙烯，英文简称PVC（Polyvinylchloride)，是氯乙烯单体（vinylchloridemonomer,简称VCM）在过氧化物、偶氮化合物等引发剂；或在光、热作用下按自由基聚合反应机理聚合而成的聚合物。铝基银浆，为铝粉通过特殊的表面处理工艺与相应溶剂制成的颜料，能够对可见光反射呈银白色，使其具有良好的装饰性能和遮盖性能。但是现有技术的易刮银油墨，性能一般都不够稳定，刮除不够方便彻底，亦或是生产过程复杂，生产过程及原料不够环保。
技术实现思路
本专利技术主要解决的技术问题是提供一种PVC材料专用高遮盖环保易刮油墨，具有存储稳定、环保无毒害的特点。为解决上述技术问题，本专利技术采用的一个技术方案是：提供一种PVC材料专用高遮盖环保易刮油墨，是由下述质量分数的材料制备而成的：铝基银浆20~25%、1/8秒硝化棉树脂10~15%、无毒增塑剂1~5%、煅烧高岭土5~10%、乙酯25~30%、异丙醇25~30%。在本专利技术的一个较佳实施例中，所述铝基银浆为3305银浆，所述铝基银浆的粒径为6微本文档来自技高网...

【技术保护点】
一种PVC材料专用高遮盖环保易刮油墨，其特征在于，是由下述质量分数的材料制备而成的：铝基银浆20~25%、1/8秒硝化棉树脂10~15%、无毒增塑剂1~5%、煅烧高岭土5~10%、乙酯25~30%、异丙醇25~30%。

【技术特征摘要】
1.一种PVC材料专用高遮盖环保易刮油墨，其特征在于，是由下述质量分数的材料制备而成的：铝基银浆20~25%、1/8秒硝化棉树脂10~15%、无毒增塑剂1~5%、煅烧高岭土5~10%、乙酯25~30%、异丙醇25~30%。2.根据权利要求1所述的PVC材料专用高遮盖环保易刮油墨，其特征在于，所述铝基银浆为3305银浆，所述铝基银浆的粒径为6微米。3.根据权利要求1所述的PVC材料专用高遮盖环保易刮油墨，其特征在于，所述无毒增塑剂为柠...