一种抗菌涂料制造技术

本发明专利技术涉及一种涂料，具体的讲，是涉及一种抗菌涂料。原料及其质量百分比为：银锌二氧化钛0.2-5％，苯乙烯-苯烯酸脂共聚乳液30-40％，晶体型负离子添加剂1-5％，钛白粉颜料15-20％，硫酸钙5-20％，消泡剂0.3-1％，抗菌剂0.5%～20%，余量的去离子水。本发明专利技术抗菌材料为能与涂料均匀混合、化学稳定性好、且不改变涂料化学结构及原施工工艺的超细无机抗菌材料粉体，所采用的无机抗菌材料是指市售的以磷酸盐系、硅酸盐系、氧化物系无机材料为载体，银、铜、锌金属离子为抗菌成份的抗菌材料。

An antibacterial coating

The invention relates to a coating, in particular to an antibacterial coating. Raw materials and quality percentage: silver zinc titanium dioxide 0.2-5%, styrene benzene acrylic resin copolymer emulsion 30-40%, crystal type negative ion additive 1-5%, titanium dioxide 15-20%, calcium sulfate 5-20%, defoaming agent 0.3-1%, antibacterial agent 0.5% ~ 20%, deionized water margin. As with superfine inorganic paint uniformly mixed, good chemical stability, and does not change the original paint chemical structure and construction technology of antibacterial material powder of the invention antibacterial material, the inorganic antibacterial material refers to commercially available phosphate, silicate, oxide inorganic material as a carrier, silver, copper and zinc as the metal ion antibacterial material composition.

【技术实现步骤摘要】

本专利技术涉及一种涂料，具体的讲，是涉及一种抗菌涂料。
技术介绍
目前，公知的涂料在建筑、车辆、军事、装饰、船舶行业用量大，与人们的生活息息相关，但涂料本身没有杀菌、抗菌功能，因此在医院、厨房、卫生间及各种公共场所的涂料表面容易滋生细菌，成为病菌的传染源，影响人体健康。国际卫生组织有关调查表明，大部分传染性疾病都是由病原体感染引起的，特别是医源性感染最为普遍。因此，一些卫生清洁度要求较高的特殊场所和人群密集的公共场所对所使用的涂料有了更高的卫生方面要求，但是现在市场上普通的涂料已经无法满足这一卫生性能要求。目前，抗菌涂料中所采用的抗菌剂主要为汞盐类等无机盐，由于其自身的毒性，会对人体造成一定的伤害。
技术实现思路
针对上述技术问题，本专利技术的目的在于提供一种抗菌涂料。本专利技术采用的技术方案如下：原料及其质量百分比为：银锌二氧化钛0.2-5％，苯乙烯-苯烯酸脂共聚乳液30-40％，晶体型负离子添加剂1-5％，钛白粉颜料15-20％，硫酸钙5-20％，消泡剂0本文档来自技高网...

【技术保护点】
一种抗菌涂料，其特征在于：原料及其质量百分比为：银锌二氧化钛0.2‑5％，苯乙烯‑ 苯烯酸脂共聚乳液30‑40％，晶体型负离子添加剂1‑5％，钛白粉颜料15‑20％，硫酸钙5‑20％，消泡剂0.3‑1％，抗菌剂0.5%～20%余量的去离子水。

【技术特征摘要】
1.一种抗菌涂料，其特征在于：原料及其质量百分比为：
银锌二氧化钛0.2-5％，
苯乙烯-苯烯酸脂共聚乳液30-40％，
晶体型负离子添加剂...