The invention relates to the field of construction, in particular to a luminous composite coating for building. The technical scheme of the invention are as follows: (1) preparation of composite glue, coarse filter (2), (3) (4) mixed additives, defoaming agent, (5) add mosquito expelling agent, (6): the prepared products with good paint cans. The invention has the advantages of simple manufacturing process, low cost, suitable for inner wall spraying, spraying can also be applied to the wall paint, not easy to fall off, waterproof and antifouling effect is good, non-toxic, tasteless, no pollution. The construction is safe and simple and the construction time is short. The coating is excellent in toughness, strength, elasticity, weather resistance and durability.
【技术实现步骤摘要】
本专利技术涉及建筑领域，具体的讲，是涉及一种建筑用夜光复合涂料。
技术介绍
建筑涂料具有装饰功能、保护功能和居住性改进功能。建筑复合涂料主要有两种复合形式，一种是两类涂料在品种上的复合，另一种则是两类涂料的涂层的复合装饰。两类涂料在品种上的复合就是把水性有机树脂与水溶性硅酸盐等配制成混合液或分散液（例如聚乙烯醇水玻漓涂料和苯丙一硅溶胶涂料等），或者是在无机物的表面上使用有机聚合物接枝制成悬浮液。这类建筑复合涂料中的有机聚合物或者树脂可以改善无机材料（例如硅溶胶）在成膜后发硬变脆的弊端，同时又避免或减轻了有机材料易老化、不耐污染、耐热性差等问题。两类涂料的涂层的复合装饰是指在建筑物的墙面上先涂覆一层有机涂料的涂层，然后再涂覆一层无机涂料涂层，利用两层涂膜的收缩不同，使表面一层无机涂料涂层形成随机分布的裂纹纹理，以便得到镶嵌花纹状涂膜的装饰效果。
技术实现思路
针对上述技术问题，本专利技术的目的在于提供一种建筑用夜光复合涂料。本专利技术采用的技术方案如下：（1）配制复合胶水：将水玻璃和水溶性脲醛树脂胶按1：3的比例混合，并按胶用量20％配制加水，在高温100℃下溶化为液体以备用；（2）粗滤：胶水制备好后进行粗滤，过滤到搅拌槽内，—边搅拌边加入滑石粉，轻质碳酸钙，石灰浆；（3）混合添加剂：按比例加添加剂、助剂，增稠剂、分散剂，防沉降剂，然后放在高速搅拌机搅拌3小时；（4）添加消泡剂：如涂料混合均匀后，若泡泡太多可加少量消泡剂再搅拌10分钟即能消除；（5）添加驱除蚊虫试剂：加入氨...
【技术保护点】
建筑用夜光复合涂料，其特征在于：具体制备过程为：（1）配制复合胶水：将水玻璃和水溶性脲醛树脂胶按1 ：3 的比例混合，并按胶用量 20 ％配制加水，在高温100 ℃下溶化为液体以备用；（2）粗滤： 胶水制备好后进行粗滤，过滤到搅拌槽内，—边搅拌边加入滑石粉，轻质碳酸钙，石灰浆； （3）混合添加剂： 按比例加添加剂、助剂，增稠剂、分散剂，防沉降剂，然后放在高速搅拌机搅拌3小时；（4）添加消泡剂：如涂料混合均匀后，若泡泡太多可加少量消泡剂再搅拌10 分钟即能消除； （5）添加驱除蚊虫试剂：加入氨基甲酸酯，搅拌均匀；（6）制得成品：把配好的涂料装罐。
【技术特征摘要】
1.建筑用夜光复合涂料，其特征在于：具体制备过程为：
（1）配制复合胶水：将水玻璃和水溶性脲醛树脂胶按1：3的比例混合，并按胶用量20％配制加水，在高温100℃下溶化为液体以备用；
（2）粗滤：胶水制备好后进行粗滤，过滤到搅拌槽内，—边搅拌边加入滑石粉，轻质碳酸钙，石灰浆；
...