The invention discloses an antibacterial fabric preparation process, after finishing of fabrics and Fabric Antibacterial preparation, preparation of complete ecological antibacterial fabric; the utility model has the advantages of adding dopamine in the finishing liquid, the polydopamine films formed on the fabric, with good adhesion properties and the reduction in the moist environment, not to join the other reducing agent, by one step impregnation process silver ions on the surface of the fabric in situ reduction of silver nanoparticles, preparation of antibacterial fabric, made of silver particles of good fastness, preparation of antibacterial fabric durability.
【技术实现步骤摘要】
一种抗菌织物的制备工艺
本专利技术属于纺织生产
,具体涉及一种抗菌织物的制备工艺。
技术介绍
随着科技的发展和人类生活水平的日益提高,人们对身体的健康和生活的便捷越来越关注。因此,工作环境及日用品的健康化已成为当今时代的发展潮流,银作为一种高效的抗菌剂己经被使用了很多年。它具有广谱的杀菌性能、对人体低毒,特别是在伤口的愈合方面起到了很大的作用。由于具有很好的杀菌特性银己被商业化应用。将纳米银抗菌剂加入到纤维聚合物单体或纺丝原液中,首先制备具有抗菌性能的纺丝原液,再通过纺丝设备进行纺丝,制成具备抗菌性能的纤维进而加工成具有抗菌性能的织物。纤维改性法制备抗菌纤维的优点是耐洗涤性能好,抗菌效果比较持久,但是成本较高,且应用范围也较窄,仅适用于涤纶、锦纶等通过纺丝工艺制备的合成纤维。
技术实现思路
本专利技术的目的在于针对现有技术的不足,现提供一种操作简单,适应范围广的抗菌织物的制备工艺。为了解决上述技术问题,本专利技术的技术方案为:一种抗菌织物的制备工艺,其创新点在于:经过织物的整理和抗菌织物的制备,完成抗菌织物的制备工艺,所述具体步骤如下:(1)织物的整理:将织物浸泡在多巴胺溶液中,加入三羟甲基氨基甲烷缓冲液,调pH值,超声震荡;(2)抗菌织物的制备:在22-26℃条件下,将整理之后的织物浸渍在硝酸银溶液中,之后用22-26℃清水洗涤,对洗涤之后的织物进行真空干燥,完成抗菌织物的制备。进一步的,所述步骤(1)中的多巴胺浓度为2-10g/L,pH为8-9,超声震荡时间为12-24h,超声震荡温度为20-28℃,超声机功率400-1000w。进一步的,所述步骤( ...
【技术保护点】
一种抗菌织物的制备工艺,其特征于:经过织物的整理和抗菌织物的制备,完成抗菌织物的制备工艺,所述具体步骤如下:(1)织物的整理:将织物浸泡在多巴胺溶液中,加入三羟甲基氨基甲烷缓冲液,调pH值,超声震荡;(2)抗菌织物的制备:在22‑26℃条件下,将整理后的织物浸渍在硝酸银溶液中,之后用22‑26℃的清水洗涤,对水洗后的织物进行真空干燥,完成抗菌织物的制备。
【技术特征摘要】
1.一种抗菌织物的制备工艺,其特征于:经过织物的整理和抗菌织物的制备,完成抗菌织物的制备工艺,所述具体步骤如下:(1)织物的整理:将织物浸泡在多巴胺溶液中,加入三羟甲基氨基甲烷缓冲液,调pH值,超声震荡;(2)抗菌织物的制备:在22-26℃条件下,将整理后的织物浸渍在硝酸银溶液中,之后用22-26℃的清水洗涤,对水洗后的织物进行真空干燥,完成抗菌织物的制备。2.根据权利要求1所述的一种抗菌织物的制备工艺...