The invention relates to the technical field of refrigeration preservation reagent, especially relates to a refrigerator evaporator with aluminum anticorrosive paint and preparation method thereof, a refrigerator evaporator with aluminum paint, the components and weight ratio: vinyl end silicone oil co polyacrylic acid resin 20 ~ 35, 20 ~ 45 flake zinc powder samples from 10 to 20, spherical zinc, phosphorus powder is 5 ~ 10, organic bentonite is 1 ~ 2, butyl acetate is 15 ~ 20, 110 epoxy resin 120, 22, 10 amino resin modified bisphenol epoxy resin 10 20 copies, 10 novolac epoxy resin 20, Zinc Oxide 2 slice 10 copies, 50 copies of 30 vinyl chloride. The anticorrosive coating of the invention is used for aluminum sheets, and has the advantages of stable performance, strong adhesion, no peeling, shock resistance, no toxic side effects, safe and environmental protection, and clean and lustrous surface after use.
【技术实现步骤摘要】
一种冰箱蒸发器用铝板防腐漆及其制备方法
本专利技术涉及制冷防腐试剂
，尤其涉及一种冰箱蒸发器用铝板防腐漆及其制备方法。
技术介绍
铝板是制冷行业中蒸发器用量较为大原材料，现有普通的铝板在制作蒸发器时都需要将其表面进行处理，以提高产品的防腐性。现有铝板防腐涂料配方设计不合理，防腐涂料层性能不稳定，附着力不强，容易脱落，不耐冲击，产品整体表面不够光泽，应用于冷柜制冷系统内衬时，使用寿命短。
技术实现思路
本专利技术的目的是提供了一种冰箱蒸发器用铝板防腐漆，防腐涂料层性能稳定，附着力强，不脱落，耐冲击，无毒副作用，安全环保，使用后产品表面整洁、光泽。为解决上述技术问题，本专利技术采取如下技术方案：一种冰箱蒸发器用铝板防腐漆，其组分及重量份配比如下：端乙烯基硅油共聚丙烯酸树脂为20～35份，鳞片状锌粉为20～45份，球状锌粉为10～20份，磷铁粉为5～10份，有机膨润土为1～2份，乙酸丁酯为15～20份，环氧树脂110-120份、氨基树脂10-22份、改性双酚环氧树10-20份、酚醛环氧树脂10-20份、氧化锌薄片2-10份、氯乙烯30-50份。一种冰箱蒸发器用铝板防腐...
【技术保护点】
一种冰箱蒸发器用铝板防腐漆，其特征在于：其组分及重量份配比如下：端乙烯基硅油共聚丙烯酸树脂为20～35份，鳞片状锌粉为20～45份，球状锌粉为10～20份，磷铁粉为 5 ～ 10份，有机膨润土为1～2份，乙酸丁酯为 15 ～ 20份，环氧树脂 110‑120 份、氨基树脂10‑22份、改性双酚环氧树10‑20份、酚醛环氧树脂10‑20份、氧化锌薄片2‑10份、氯乙烯30‑50份。
【技术特征摘要】
1.一种冰箱蒸发器用铝板防腐漆，其特征在于：其组分及重量份配比如下：端乙烯基硅油共聚丙烯酸树脂为20～35份，鳞片状锌粉为20～45份，球状锌粉为10～20份，磷铁粉为5～10份，有机膨润土为1～2份，乙酸丁酯为15～20份，环氧树脂110-120份、氨基树脂10-22份、改性双...
【专利技术属性】
技术研发人员：时乾中，肖翔，王玉珏，王子俊，
申请(专利权)人：合肥太通制冷科技有限公司，
类型：发明
国别省市：安徽,34