The utility model discloses a built-in aluminum carbon submerged nozzle, including the nozzle body made of aluminum carbonaceous material (1), which is characterized in that the outer wall of the nozzle body (1) is coated with a thickness of 0.1 ~ 1mm oxidation resistant glaze layer (2); anti oxidation layer of the glaze (2) along the nozzle body (1) of the bowl lateral nozzle body (1) of the extending spray. The utility model through the outer wall of the nozzle body is coated with a thickness of 0.1 to 1mm oxidation resistant glaze layer, the oxidation resistant glaze layer formation of liquid in the oxidizing atmosphere of 800 DEG -1250 DEG under the glass phase, thereby protecting the nozzle body by oxidation, continuous casting to ensure the long time; the install the submerged nozzle due to oxidation of the glaze layer of high strength, convenient in installation and operation in the process of handling, high security, high speed and long time to meet the requirements of cast steel.
【技术实现步骤摘要】
本技术涉及板坯薄板坯连铸
，具体地说是一种可以保证长时间烘烤和长浇次连续浇铸的铝碳质内装浸入式水口。
技术介绍
连铸技术在我国已经发展了几十年，对钢液的保护浇注措施也是多种多样。对于常规板坯，为了延长中间包的单包使用寿命，通常采用水口快换的方式，有的是使用内装浸入式水口。特别是近几年来我国在薄板坯连铸连轧方面，对内装浸入式水口的使用时间也越来越高。对于内装浸入式水口，水口的上部通常有一部份直接跟中间包散料（填充料）接触，当中间包采用喷涂料或手抹料时，喷涂料或手抹料中的水份就会通过填充料向水口本体内渗透，在高温状态下，会与水口中的材料发生化学反应，水口发生反应之后，会造成产品表面氧化、强度和抗侵蚀性能急剧下降，很容易出现事故。浸入式水口为等静压成型的铝碳质制品，铝碳质耐火材料的结合方式是通过材料本体中的石墨形成脉状网络结合在一起，而石墨和碳很容易在烘烤和浇铸过程中被氧化。
技术实现思路
本技术的目的是针对现有铝碳质内装浸入式水口易被氧化的问题，提供一种满足长时间连续浇钢、连铸效率高的铝碳质内装浸入式水口。本技术的目...
【技术保护点】
一种铝碳质内装浸入式水口，包括采用铝碳质材料制成的水口本体（1），其特征在于所述水口本体（1）的外壁上喷涂有厚度为0.1～1mm的防氧化釉层（2）；所述的防氧化釉层（2）沿水口本体（1）的碗部下侧向水口本体（1）的下部延伸喷涂。
【技术特征摘要】
1.一种铝碳质内装浸入式水口，包括采用铝碳质材料制成的水口本体（1），其特征在于所述水口本体（1）的外壁上喷涂有厚度为0.1～1mm的防氧化釉层（2）；所述的防氧化釉层（2）...