The preparation process of the present invention relates to a medical starch acrylic composite hydrogel, mainly composed of gelatinized starch, acrylic acid, 15-20% with alkali neutralization of 12-16% after N, N '- methylene bis acrylamide, 20-40% distilled water monomer, 45-55% monomer and 20-25% ammonium persulfate and 12-16% N, N' - methylene bis acrylamide through reaction, freezing and thawing, so the cycle 6 times prepared. The reasonable preparation conditions and composition, with physical and chemical methods to complete the medical starch acrylic based composite hydrogel preparation method, low cost, the hydrogel is not easy to change color, moisturizing effect is good, use time more than 720 hours and germproof antivirus, suitable for medical dressing.
【技术实现步骤摘要】
本专利技术涉及一种医用淀粉丙烯酸基复合水凝胶的制备工艺，属于医用复合敷料制备
本专利技术由淀粉、分析纯丙烯酸、过硫酸铵、N，N′-亚甲基双丙烯酸胺制备而成，可用于有黄色腐肉和黑色坏死组织的伤口的自溶清创，少至中量渗液的伤口，烧伤和放射性伤口以及骨膜、筋腱暴露的伤口，具有保湿、不易变色、抗菌消炎、促进伤口愈合，有利于上皮移行及肉芽生长等作用，对正常皮肤还可产生润肤护肤、延缓皮肤细胞衰老等功效。
技术介绍
医用敷料按采用的材料目前大致可分为：天然材料类，合成高分子材料类，复合材料类、组织工程类等。天然材料又包括棉纤维、甲壳素/壳聚糖、海藻酸盐、明胶、胶原、动物皮、同种自体/异体皮。天然材料制成的敷料大部分吸收性好，具有良好的生物相容性及生物学活性，但是机械性能差。如传统的棉纱敷料吸收能力有限，在使用时无法保持创面愈合所需的湿润环境，延迟创面愈合。而且容易粘连伤口，在换药时不仅会引起疼痛，还会造成二次损伤。壳聚糖膜敷料存在力学性能差、脆性较大、抗水性差等缺点。海藻酸盐使用时...
【技术保护点】
一种医用淀粉丙烯酸基复合水凝胶的制备工艺，其特征在于具有如下制备工艺：(1)将淀粉加入到装有搅拌器、冷凝管、温度计的烧瓶中，加入20％的蒸馏水，于85℃恒温水浴中糊化35min；(2)在烧杯中放入适量的丙烯酸，水浴冷却；搅拌下滴入25％氢氧化钠溶液中和至Ph值5～7；(3)按称取12％的N，N′‑亚甲基双丙烯酸胺和15％部分中和后的丙烯酸置于烧杯中，加入20％的蒸馏水，搅拌混合均匀；(4)淀粉糊化结束后，量取40％蒸馏水，放入三口瓶中，在恒温油浴上加热，温度恒定在70℃左右，加入52％的单体和23％过硫酸铵溶液及12％的N，N′‑亚甲基双丙烯酸胺，搅拌直至恒温后，使其反应2...
【技术特征摘要】
1.一种医用淀粉丙烯酸基复合水凝胶的制备工艺，其特征在于具有如下制备工艺：
(1)将淀粉加入到装有搅拌器、冷凝管、温度计的烧瓶中，加入20％的蒸馏水，于85℃
恒温水浴中糊化35min；
(2)在烧杯中放入适量的丙烯酸，水浴冷却；搅拌下滴入25％氢氧化钠溶液中和至Ph
值5～7；
(3)按称取12％的N，N′-亚甲基双丙烯酸胺和15％部分中和后的丙烯酸置于烧杯中，加入
20％的蒸馏水，搅拌混合均匀；
(4)淀粉糊化结束后，量取40％蒸馏水，放入三口瓶中，在恒温油浴上加热，温度恒定
在70℃左右，加入52％的单体和23％过硫酸铵溶液及12％的N，N′-亚甲基...