The invention discloses a silk pad refining method, which comprises the following steps: 1) mixing liquid padding, blank silk padding mixing liquid, under the control of the 90-100% between the rate of rolling liquid; 2) at room temperature in the stack, slowly rotating under the condition of room temperature stacking 10-30 hours; 3) with high temperature washing. Alkali agent and cationic surfactant, the cold rolling process of hydrolysis of sericin, impurities, from the fabric by emulsification, dispersion in 60-70 C water cleaning, and finally washing clean. The invention has the advantages of obvious water saving and energy saving compared with the existing method, and the corresponding waste water is obviously reduced, and the environmental protection effect is good.
【技术实现步骤摘要】
本专利技术涉及一种真丝冷轧堆炼方法。
技术介绍
通常真丝绸炼自采用高温浸泡、初炼、复炼等方法，另外还有少量高温平幅连续式快速精炼方法，这两种方法都要消耗大量的水、能源，同时产生大量废水，造成环境污染。
技术实现思路
本专利技术所要解决的技术问题是：提供一种真丝冷轧堆炼方法。为解决上述技术问题，本专利技术采用的技术方案是：一种真丝冷轧堆炼方法，其特征在于包括如下步骤：1），浸轧炼液，坯绸浸轧炼液，轧液率控制在90-100%之间；2），室温堆置，在慢速转动的状态下，室温堆置10-30个小时；3），高温洗涤，用碱剂和阳离子表面活性剂，将冷轧堆工序中水解的丝胶、杂质，从织物上通过乳化，分散在60-70℃水中清洗除去，最后水洗干净。本专利技术的有益效果是：比现有方法可明显节水、节能，产生的废水也相应明显减少，环保效果良好。具体实施方式实施例1一种真丝冷轧堆炼方法，其特征在于包括如下步骤：1），浸轧炼液，坯绸浸轧炼液，轧液率控制在100%之间；2），室温堆置，在慢速转动的状态下，室温堆置30个小时；3），高温洗涤，用碱剂和阳离子表面活性剂，将冷轧堆工序中水解的丝胶、杂质，从织物上通过乳化，分散在70℃水中清洗除去，最后水洗干净。实施例2一种真丝冷轧堆炼方法，其特征在于包括如下步骤：1），浸轧炼液，坯绸浸轧炼液，轧液率控制在90%之间；2），室温堆置，在慢速转动的状态下，室温堆置10个小时；3），高温洗涤，用碱剂和阳离子表面活性剂，将冷轧堆工序中水解的丝胶、杂质，从织物...
【技术保护点】
一种真丝冷轧堆炼方法，其特征在于包括如下步骤：1），浸轧炼液，坯绸浸轧炼液，轧液率控制在90‑100%之间；2），室温堆置，在慢速转动的状态下，室温堆置10‑30个小时；3），高温洗涤，用碱剂和阳离子表面活性剂，将冷轧堆工序中水解的丝胶、杂质，从织物上通过乳化，分散在60‑70℃水中清洗除去，最后水洗干净。
【技术特征摘要】
1.一种真丝冷轧堆炼方法，其特征在于包括如下步骤：1），浸轧炼液，坯绸浸轧炼液，轧液率控制在90-100%之间；2），室温堆置，在慢速转动的状态下，室温堆置10...