The invention discloses an aging treatment method for improving performance of GH2132 high temperature lasting bolt, the bolt GH2132 in the existing solid after the dissolution process and an aging process adds another aging process, smaller size and greater dispersion of gamma prime strengthening phase to get through the second aging process, improve the bolt enduring high temperature the performance and fatigue life of the bolt. The invention adds an aging process after the existing GH2132 bolt processing technology, so that the high-temperature endurance performance of the GH2132 bolt is greatly improved, and the fatigue performance and the use safety are guaranteed. Thus successfully solved the technical problems that the grain temperature and the high temperature can not be guaranteed at the same time when the conventional heat treatment is produced. Therefore, the invention can be popularized in the field of GH2132 bolts for Aero engines.
【技术实现步骤摘要】
一种提高GH2132螺栓高温持久性能的时效处理方法
本专利技术涉及一种提高GH2132螺栓高温持久性能的时效处理方法，属于航空发动机GH2132螺栓时效处理工艺
技术介绍
现代高温合金，包括铁基、镍基、钴基高温合金，其中GH2132是我国试制的铁基时效沉淀硬化型高温合金。该合金在苏系或俄系材料中没有相应牌号，是通过仿制美系发动机而试制的材料，相当于美系A286高温合金。该材料在650℃以下具有高的屈服强度和持久、蠕变强度，并具有较好的加工塑性和满意的焊接性能。在国内该合金已在航空领域获得较为广泛的应用，适合制造在650℃以下长期工作的航空发动机高温承力部件，如涡轮盘、压气机盘、转子叶片和高温紧固件等。用GH2132制造的航空发动机螺栓，主要起连接和紧固各相关零部件作用，而GH2132螺栓高温持久性能的高低直接影响到发动机的使用寿命。目前已有型号的GH2132螺栓，其技术要求为：1）室温抗拉≥900MPa；2）硬度27～35HRC；3）应力断裂试验650℃、加载480MPa、保持23h不断；4）晶粒度≥5级，不允许有粗细晶粒带存在。没有提出高温强度指标和疲...
【技术保护点】
一种提高GH2132螺栓高温持久性能的时效处理方法，其特征在于：所述GH2132螺栓在现有的固溶工艺和一道时效工艺之后再增加一道时效工艺，通过第二道时效工艺来获得尺寸更小、弥散度更大的γ′强化相，提高螺栓高温持久性能和螺栓疲劳寿命。
【技术特征摘要】
1.一种提高GH2132螺栓高温持久性能的时效处理方法，其特征在于：所述GH2132螺栓在现有的固溶工艺和一道时效工艺之后再增加一道时效工艺，通过第二道时效工艺来获得尺寸更小、弥散度更大的γ′强化相，提高螺栓高温持久性能和螺栓疲劳寿命。2.根据权利要求1所述提高GH2132螺栓高温持久性能的时效处理方法，其特...
【专利技术属性】
技术研发人员：樊开伦，裴烈勇，陈涛，刘勇德，徐韬，
申请(专利权)人：贵州航天精工制造有限公司，
类型：发明
国别省市：贵州,52