The invention relates to a building coating, in particular to an inorganic ceramic coating used for building walls or decorative boards. It contains the weight and ratio of aqueous silica sol is 34 ~ 56%, 26 ~ 46% alumina or alumina hydrate, water soluble amine 1 ~ 7%, calcium oxide or calcium hydroxide from 2 to 13%, the rest is water. The invention can make a variety of building materials (such as ceramic, glass, concrete and calcium silicate board) coating has good adhesion, and coating obtained has excellent hardness, water resistance, stain resistance, acid and alkali resistance, no burning, easy to use, can be widely used in building facades and decorative board.
【技术实现步骤摘要】
一种无机陶瓷涂料
本专利技术涉及一种建筑涂料，尤其是涉及一种用于建筑物墙体或装饰板的无机陶瓷涂料。
技术介绍
无机建筑涂料的开发与应用始于20世纪70年代初期石油危机出现后，市场上需求一种更加经济耐用的涂料。当时，日本首先成功研究开发了以硅酸盐无机高分子为成膜物质的涂料，德国的BASF、Wacker、Bayer和Keimfarben等公司，也先后研制出了以特制液态硅酸钾为主要成膜物质的新型无机涂料。此后，美国在无机涂料、无机～有机复合涂料方面也有了较快发展。到20世纪80年代初以来，我国也有这类涂料研究成功的报道，主要是以硅酸钠、硅酸钾为基料的无机涂料，和硅溶胶-苯丙树脂为基料的无机涂料。以碱金属硅酸盐为基料的无机涂料，涂膜的物化性能，包括保光性、保色性、耐黄变性、耐热性、耐冻性和耐冻融循环性等都较好，尤其长期置于大气环境中几乎不黄变。同时，此类涂料的耐化学及耐腐蚀性能，包括耐石油制品性、耐溶剂性、耐家用化学品性和耐化工气体性等。但由于碱金属硅酸盐类易溶于水，此类无机涂料用于建筑物外墙的最大问题就是涂膜耐水性不佳，时间长易风化、开裂。硅溶胶-苯丙树脂为基料的无机涂...
【技术保护点】
一种无机陶瓷涂料，其特征是：它含有的重量组分及配比为硅溶胶27～ 62％，氧化铝或水合氧化铝20～37％，水溶性醇胺1～7％，氧化钙或氢氧化钙 2～13％，颜料5～16％，高分子量聚氨酯分散剂0.5～2％，其余为水。
【技术特征摘要】
1.一种无机陶瓷涂料，其特征是：它含有的重量组分及配比为硅溶胶27～62％，氧化铝或水合氧化铝20～37％，水溶性醇胺1～7％，氧化钙或氢氧化钙2～13％，颜料5～16％，高分子量聚氨酯分散剂0.5～2％，其余为水。2.根据权利要求1所述的一种无机...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。