The invention discloses a clay mold semi-finished antifreeze, aiming to provide a mold for antifreeze harmless and low cost, the technical scheme is as follows: with 0.8 calcium chloride and 0.2 sodium chloride combo, the amount may be as high and low temperature, it first soaked in water after melting is more better even, also can be added directly, its content is: - 8 (minus 8 degrees, the same below), adding amount of raw materials 1 per thousand; - 12, amount of raw materials for 1 +%; - 17, amount of raw materials for 1.5 +% - 22, was added; 2 of the raw materials% +; - 27, amount of raw materials for 2.5 +%; - 32, 3 +% is added to raw materials.
【技术实现步骤摘要】
粘土原料坯胎防冻剂
本专利技术涉及选用粘土为原料制做的陶瓷半成品及砖瓦坯胎的一种防冻裂添加剂，更确切更具体地讲是涉及当气温降至零下几度时在原料中掺入一定数量的化工原料以防坯胎受冻害而报废的一种防冻剂。
技术介绍
现有技术即传统作法当天气寒冷时，在坯料中加入一定成份的氯化纳，从泛霜方面看很有害，因为坯胎干是要通过高温焙烧才能成为成品，加入氯化纳的坯胎在焙烧过程中可转化为硫酸纳而影响美观，并成本较高。专利技术內容本专利技术为克服上述不足，旨在提供一种对坯胎无害且成本低的防冻剂，选用以下技术方案予以实现。选用价廉的氯化钙为总成份的0.8，氯化纳为总成份的0.2，其加入量视气温高低而定，先将其浸于水中溶化后效果更佳即更为均匀，直接加入也是可以的，其加入量为：—8（零下8°，下同），加入量为原料的1‰；—12，加入量为原料的1‰+-；—17，加入量为原料的1.5‰+-；—22，加入量为原料的2‰+-；—27，加入量为原料的2.5‰+-；—32，加入量为原料的3‰+-。
【技术保护点】
一种粘土坯胎半成品防冻剂，其特征是：选用0.8的氯化钙和0.2的氯化钠，其加入量视气温高低而定，先将其浸于水中溶化后效果更佳即更为均匀，直接加入也是可以的，其加入量为：—8（零下8°，下同），加入量为原料的1‰；—12，加入量为原料的1‰+‑；—17，加入量为原料的1.5‰+‑；—22，加入量为原料的2‰+‑；—27，加入量为原料的2.5‰+‑；—32，加入量为原料的3‰+‑。
【技术特征摘要】
1.一种粘土坯胎半成品防冻剂，其特征是：选用0.8的氯化钙和0.2的氯化钠，其加入量视气温高低而定，先将其浸于水中溶化后效果更佳即更为均匀，直接加入也是可以的，其加入量为：—8（零下8°，下同...