The present invention relates to a waterproof rubber sleeve and preparation method and use the ad traffic lights of the waterproof rubber sleeve; including waterproof rubber sleeve, a vertical rod, and the suit used in waterproof rubber sleeve inside the billboard; the central pole is provided with a lamp holder with a protective shell, the pole of the upper and lower ends are respectively provided with a hollow supporting rod, a hollow outer surface of the supporting rod is arranged on the maintenance door, one side upper part of the upright rod support rod is provided with waterproof rubber sleeve the billboard, top billboard is provided with a support bar rod connected, a plurality of connecting rods are arranged between the bar and the advertisement board; the lamp socket is provided with a red light, the green and yellow light; has the advantages of reasonable design, high accuracy and long service life, and is used to protect the waterproof rubber sheath billboard is not easy to harden, waterproof and not easy to break the advantages.
【技术实现步骤摘要】
本专利技术属于动画广告式交通信号灯
,具体涉及一种防水胶套及制备方法和使用该防水胶套的广告交通信号灯。
技术介绍
交通信号灯是交通指挥中的重要组成部分,是道路交通的基本语言。交通信号灯由红灯表示禁止通行、绿灯表示允许通行、黄灯表示警示组成。分为:机动车信号灯、非机动车信号灯、人行横道信号灯、车道信号灯、方向指示信号灯、闪光警告信号灯、道路与铁路平面交叉道口信号灯,是道路交通不可缺少的工具。另外,现有的广告无处不在,在马路上,广告的信息总是能够出现在人们的视线,再者,在一些市中心的主要路段,交通信号灯的间隔时间通常在2分钟内,而在这两分钟内,足够一些商家对自身商品进行广告,能够弥补司机或者乘客在等红绿灯这两分钟的真空期,但是现有的交通信号灯要么只是简简单单的红黄绿三个指示灯座,无广告牌,要么直接在交通信号灯上挂上广告牌进行广告,但是直接把广告牌安装在交通信号灯上,只能对单一的商品进行宣传,其形式单一,不够形象生动。此外,即使一些具有广告功能的交通信号灯,其在使用时,由于是露天安置,容易损坏,导致辨识度低和寿命短,用于保护广告牌的外壳硬化快、易渗水和易断裂的问题。
技术实现思路
本专利技术的目的就在于为了解决上述问题而提供一种用于保护广告牌、具有不易硬化、防渗水和不易断裂的防水胶套和设计合理、辨识度高和寿命长的防水胶套及制备方法和使用该防水胶套的广告交通信号灯。本专利技术通过以下技术方案来实现上述目的:(一)一种防水胶套,该防水胶套包括下列重量份数的原料制成:甲基乙烯基硅橡胶30-40份、丁苯橡胶28-36份、炭黑11-17份、氧化锌10-14份、硬脂酸1 ...
【技术保护点】
一种防水胶套,其特征在于:该防水胶套包括下列重量份数的原料制成:甲基乙烯基硅橡胶30‑40份、丁苯橡胶28‑36份、炭黑11‑17份、氧化锌10‑14份、硬脂酸13‑15份、勃姆石7‑11份、钼酸钠5‑9份、镍粉4‑6份、铌粉4‑6份、锆粉4‑6份、碳粉4‑6份、锰粉4‑6份、3‑戊二醇二双异丁酸酯增塑剂1‑3份、钙锌稳定剂2‑4份、抑烟剂4‑8份、二甲基硅油5‑7份和聚醚胺催化剂3‑5份;所述的抑烟剂为膨胀型红磷、氢氧化镁、氢氧化铝或茂金属聚丙烯中的一种或一种以上的混合物。
【技术特征摘要】
1.一种防水胶套,其特征在于:该防水胶套包括下列重量份数的原料制成:甲基乙烯基硅橡胶30-40份、丁苯橡胶28-36份、炭黑11-17份、氧化锌10-14份、硬脂酸13-15份、勃姆石7-11份、钼酸钠5-9份、镍粉4-6份、铌粉4-6份、锆粉4-6份、碳粉4-6份、锰粉4-6份、3-戊二醇二双异丁酸酯增塑剂1-3份、钙锌稳定剂2-4份、抑烟剂4-8份、二甲基硅油5-7份和聚醚胺催化剂3-5份;所述的抑烟剂为膨胀型红磷、氢氧化镁、氢氧化铝或茂金属聚丙烯中的一种或一种以上的混合物。2.根据权利要求1所述的防水胶套,其特征在于:该防水胶套包括下列重量份数的原料制成:甲基乙烯基硅橡胶33份、丁苯橡胶35份、炭黑12份、氧化锌11份、硬脂酸14.5份、勃姆石10份、钼酸钠8份、镍粉4份、铌粉6份、锆粉5.5份、碳粉4.5份、锰粉4份、3-戊二醇二双异丁酸酯增塑剂3份、钙锌稳定剂4份、抑烟剂5份、二甲基硅油7份和聚醚胺催化剂5份;所述的抑烟剂为茂金属聚丙烯。3.根据权利要求1所述的防水胶套,其特征在于:该防水胶套包括下列重量份数的原料制成:甲基乙烯基硅橡胶39份、丁苯橡胶29份、炭黑15份、氧化锌13份、硬脂酸13.5份、勃姆石9份、钼酸钠6份、镍粉5.6份、铌粉5份、锆粉4份、碳粉5份、锰粉6份、3-戊二醇二双异丁酸酯增塑剂1份、钙锌稳定剂3份、抑烟剂7份、二甲基硅油6.7份和聚醚胺催化剂4份;所述的抑烟剂为膨胀型红磷、氢氧化镁和氢氧化铝的混合物。4.根据权利要求1所述的防水胶套,其特征在于:该防水胶套包括下列重量份数的原料制成:甲基乙烯基硅橡胶38份、丁苯橡胶30份、炭黑13份、氧化锌10份、硬脂酸15份、勃姆石7份、钼酸钠9份、镍粉6份、铌粉4份、锆粉6份、碳粉6份、锰粉4.5份、3-戊二醇二双异丁酸酯增塑剂2份、钙锌稳定剂2份、抑烟剂6份、二甲基硅油5.5份和聚醚胺催化剂4.5份;所述的抑烟剂为氢氧化铝和茂金属聚丙烯的混合物。5.一种如权利要求1-4任一项所述的防水胶套的制备方法,其特征在于:包括如下步骤:1)取甲基乙烯基硅橡胶、丁苯橡胶、硬脂酸、抑烟剂和聚醚胺催化剂放入反应釜内,并将反应釜的温度逐渐加热至180-220℃,使得甲基乙烯基硅橡胶和丁苯橡胶在反应釜内通过硬脂酸活化以及通过聚醚胺催化剂进行催化反应而迅速熔化成胶液,并通过抑烟剂降低甲基乙烯基硅橡胶和丁苯橡胶加热熔融产生的烟体,制得母胶混合液体,备用;2)取炭黑、氧化锌、勃姆石和钼酸钠通过研磨机反复研磨...