The invention discloses an artificial stone culture mold glue and preparation method thereof, wherein the rubber mold is composed of 90 to 94 parts by weight of group A, 6 to 10 parts by weight of group B and 0.3 to 0.5 parts by weight of catalyst, 10 to 30 parts by weight of hyperbranched organosilicon resin composition; wherein: a room temperature curing silicone rubber containing vinyl or propenyl groups, the component B is hydrogen containing polysiloxane, hyperbranched organosilicon resin as the solid content of more than 95%, the viscosity is 500 ~ 1200 centipoise, weight average molecular weight is 1600 ~ 8000 of the non solvent epoxy modified silicone resin. The mold glue is prepared by mixing each component in proportion at first, then pouring into the mold after vacuum exhaust, and curing at 90~130 DEG C. The heat shrinkage rate of the artificial stone mold adhesive obtained by the invention is obviously reduced, and the mechanical property and the thermal stability property are remarkably improved.
【技术实现步骤摘要】
本专利技术涉及一种人造文化石模具胶及其制备方法，具体说，是涉及一种由超支化有机硅树脂改性的人造文化石模具胶及其制备方法，属于硅橡胶材料
技术介绍
人造文化石是采用硅钙、石膏等材料精制而成，它模仿天然石材的外形纹理，具有质地轻、色彩丰富、不霉、不燃、便于安装等特点。人造文化石在大众装修中的应用越来越多，不但数量增加，种类也日益增多，从而带动人造文化石模具胶的需求。室温硫化硅橡胶（简称为RTV）是一种高分子弹性体，它是以硅原子和氧原子为骨架的合成材料，每个硅原子上含有1～2个有机基团（主要是甲基-CH3），是一种带有Si-O-Si链带的纤维状高分子聚合物。RTV具有以下性质：良好的化学稳定性、无毒、无腐蚀性；流动性好，能自动充满模具；可控制硫化速度，室温常压下硫化，便于操作良好的脱模性；仿真性强，纹饰逼真；制模速度快，一般20小时内即可制成模具。但人造文化石生产企业在长期使用过程中发现：在高温高湿条件下，由RTV制造的RTV模具的热收缩率较大，影响了人造...
【技术保护点】
1.一种人造文化石模具胶，其特征在于，由以下组分按如下配比组成：其中，所述的甲组份为含乙烯基或丙烯基端基的室温硫化硅橡胶生胶，所述的乙组份为含氢聚硅氧烷，所述的超支化有机硅树脂为固含量＞95%、粘度为500～1200厘泊、重均分子量为1600～8000的无溶剂型环氧改性有机硅树脂。
【技术特征摘要】
1.一种人造文化石模具胶，其特征在于，由以下组分按如下配比组成：
其中，所述的甲组份为含乙烯基或丙烯基端基的室温硫化硅橡胶生胶，所述的乙组份
为含氢聚硅氧烷，所述的超支化有机硅树脂为固含量＞95%、粘度为500～1200厘泊、重
均分子量为1600～8000的无溶剂型环氧改性有机硅树脂。
2.如权利要求1所述的人造文化石模具胶，其特征在于：所述的催化剂为含铂催化剂。
3.如权利要求2所述的人造文化石模具胶，其特征在于：所述的含铂催化剂为氯铂酸。
4.一种制备权利要求1所述的人造...
【专利技术属性】
技术研发人员：王锦成，刘瑜琦，袁章林，王军华，张广建，曹付海，
申请(专利权)人：上海工程技术大学，
类型：发明
国别省市：上海;31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。