The invention discloses a polymer rapid repair mortar, the cement, rapid hardening agent, graded sand, retarder and water reducer evenly mixed to prepare, construction to be repaired potholes to clean up after the polymer rapid repair mortar mixed with water, after mixing evenly placed in the pit, to repair mortar after the final set of water conservation, and the projecting part of Hsiuping that form a flat floor. Compared with the existing repair material, the polymer quick restoration mortar of the invention has a remarkable breakthrough in the final setting time and can be condensed after 20 minutes of repair. In addition, the polymer quick repair mortar of the invention can make the surface layer more smooth and the comprehensive performance of the application reach the optimum state without changing the original structure of the floor.
【技术实现步骤摘要】
本专利技术属于建筑材料
，具体涉及一种聚合物快速修复砂浆。
技术介绍
混凝土和钢筋混凝土作为主要的建筑材料广泛应用于各种领域。混凝土构筑物在长期的使用过程中由于设计不当、施工质量不好或使用环境的影响，如重荷载、冻融循环、氯离子的渗透、表面磨蚀，易使混凝土出现开裂、渗漏、剥落等现象，严重影响工程的使用寿命，甚至影响构筑物的安全性，因而对已损坏的混凝土进行修补是十分必要的。此外，对于路面、桥面的修补工作，由于现有道路网的交通需求，不可能允许进行长时间的封闭修复，因此，修补材料不仅要求性能良好，还需具备快速凝结的特点。混凝土修补材料目前主要有三大类：水泥类砂浆、合成树脂类砂浆和聚合物水泥砂浆。水泥类砂浆价格低廉，适宜于大面积修补，但这类修补材料粘结强度低，抗裂性和耐磨性较差，修补后受力易脱落。合成树脂类砂浆具有良好的耐久性能，粘结强度也较高，但由于与普通混凝土的弹性模量和热膨胀系数差异很大，修补后易出现老化脱落的现象，且此类材料价格较贵，使其应用受到很大限制。聚合物水泥砂浆兼具前两者的优点，具有较好的耐久性能及良好的粘结强度，但其...
【技术保护点】
聚合物快速修复砂浆，其特征在于：将水泥、快硬剂、级配砂、缓凝剂、减水剂混合均匀，即得所述聚合物快速修复砂浆。
【技术特征摘要】
1.聚合物快速修复砂浆，其特征在于：将水泥、快硬剂、级配砂、缓凝剂、减水剂混合均匀，即得所述聚合物快速修复砂浆。
2.根据权利要求1所述的聚合物快速修复砂浆，其特征在于：各组份按重量份计包括：水泥30-40份，快硬剂10-20份，级配砂40-60份，缓凝剂0.5-1份，减水剂3-5份。
3.根据权利要求1所述的聚合物快速修复砂浆，其特征在于：所述水泥为525水泥。
4.根据权利要求1所述的聚合物快速修复砂浆，其特征在于：所述级配砂的配方比为：1号砂20wt%，9号砂25wt%，石英粉25wt%，100-200...
【专利技术属性】
技术研发人员：陈遵厚，郑鸿芳，苗建程，杨喜丽，
申请(专利权)人：福州皇家地坪有限公司，
类型：发明
国别省市：福建;35