The invention provides a modification method of calcium bentonite, which comprises the following steps: calcium bentonite ground calcium bentonite powder; the modifier solution atomized and mixed with calcium bentonite powder mixed with hot air and full contact, so that the calcium bentonite powder was modified. Bentonite modified method provided by the invention adopts atomization spray technology, the calcium bentonite powder and the modifier can maximize the contact, reduces the amount of modifier, improves the modified speed, also can realize the calcium bentonite powder was completely modified the raw materials, high utilization rate, good modification effect.
【技术实现步骤摘要】
本专利技术属于工程材料领域，特别涉及一种主要是利用半干法将钙基膨润土改性为钠基膨润土的方法。
技术介绍
膨润土防水毯是主要用于人工湖泊水景、垃圾填埋场、地下车库、楼顶花园、水池、油库及化学品堆场等防渗漏的材料，主要是将高膨胀性的膨润土填充在特制的复合土工布和无纺布之间，遇水时在垫内的膨润土形成均匀高密度的胶状防水层，有效防止水的渗漏。常用的膨润土包括钙基膨润土和钠基膨润土，由于世界上钙基膨润土的分布远广于钠基膨润土，因此钙基膨润土为应用最广泛的膨润土。然而，当将钙基膨润土其膨胀仅为自身体积的3倍左右，而钠基膨润土遇水时能够吸附自身重量五倍的水，体积膨胀到原来的15-17倍以上；因此钠基防水毯的防水效果远远好于钙基膨润土做的防水毯。然而，由于钠基膨润土分布少，价格远高于钙基膨润土，因此除了加强寻找钠基膨润土外，对钙基膨润土进行改性成为钠基膨润土也不失为一种好的方法。目前对钙基膨润土进行钠化改性的方法有悬浮液法、挤压法、堆积法、轮辗法、双螺旋法、超...
【技术保护点】
一种钙基膨润土的改性方法，其特征在于：改性设备包括反应器（1）、雾化装置（2）、文丘里管（3）；所述反应器（1）侧壁设有粉料进口（4）、底部设有出料口（5）；所述雾化装置（2）包括通过进液管（8）连接的改性剂罐（6）和雾化喷嘴（7），所述雾化喷嘴（7）设于反应器（1）内，所述进液管（8）上设有加压泵（9）；所述文丘里管（3）与粉料进口（4）连接。
【技术特征摘要】
1.一种钙基膨润土的改性方法，其特征在于：改性设备包括反应器（1）、雾化装置（2）、
文丘里管（3）；所述反应器（1）侧壁设有粉料进口（4）、底部设有出料口（5）；所
述雾化装置（2）包括通过进液管（8）连接的改性剂罐（6）和雾化喷嘴（7），所述
雾化喷嘴（7）设于反应器（1）内，所述进液管（8）上设有加压泵（9）；所述文丘
里管（3）与粉料进口（4）连接。
2.根据权利要求1所述的一种钙基膨润土改性设备，其特征在于：所述雾化喷嘴（7）
的孔径为0.1～0.6mm。
3.一种钙基膨润土的改性方法，其特征在于：包括以下步骤：将钙基膨润土磨碎得钙
基膨润土粉料；将改性剂溶液雾化后与混合着热空气的钙基膨润土粉料混合并充分
接触，从而使钙基膨润土粉料被改性剂改性。
4.根据权利要求3所述的一种钙基膨润土的改性方法，其特征在于：包括以下步骤：
（1）将钙基膨润土磨碎至100目以上，得钙基膨润土粉料；
（2）将改性剂溶液经雾化装置雾...