一种利用贫锰铁矿制备锰硅合金的方法及装置制造方法及图纸
Method and device for preparing manganese silicon alloy by utilizing manganese deficient iron ore
The invention discloses a method for utilizing low-grade manganese ore preparation manganese silicon alloy, which comprises the following steps: drying and crushing the poor manganese ore; the poor manganese ore with silica fume and crushed lime mixed and the mixture balling form pellet; the pellets into the gas heating furnace melting cloth by reaction guimeng alloys. The invention also discloses a device for carrying out the method. Through the use of the method and the device, the treatment problem of low-grade manganese iron ore is solved, and the low-grade ferromanganese ore, manganese and iron are respectively recovered and utilized.
【技术实现步骤摘要】
一种利用贫锰铁矿制备锰硅合金的方法及装置
本专利技术涉及冶金领域，尤其涉及一种利用贫锰铁矿制备锰硅合金的方法及装置。
技术介绍
国内外对锰硅合金的冶炼已经有了长久而深入的研究，工艺上的改进与提高有利于各项经济难度。技术指标的提高进而达到节能降耗和提高产品质量的目的。欲使锰硅合金冶炼技术进一步提升到一个新的高度，必须对目前锰硅合金冶炼中存在的高能耗、产品质量不稳定等问题进一步解决。硅锰合金是炼钢的重要合金，使用量最大，是提高钢材力学性能的重要合金。我国每年生产铁合金约3000多万吨，其中98％的铁合金采用矿热炉生产，即使用矿热炉将矿石与焦炭加热到高温反应。矿热炉加热是通过电极将这些原料加热到高温，并需加热到1600℃以上，但这些材料导电和传热效率低，加热过程耗能大、加热速度慢，生产周期长。
技术实现思路
为了解决现有技术中存在的上述问题，本专利技术提出了一种利用贫锰铁矿制备锰硅合金的方法及装置，本专利技术利用贫锰铁矿代替高锰矿制备锰硅合金，同时解决了工业硅粉的堆存问题，充分利用硅粉的特性进行还原熔炼。本专利技术采用的方法如下：一种利用贫锰铁矿制备锰硅合金的方法，包含以下...
【技术保护点】
一种利用贫锰铁矿制备锰硅合金的方法，其特征在于，包含以下步骤：步骤一，将所述贫锰铁矿烘干并破碎；步骤二，将步骤一中破碎后的贫锰铁矿与硅粉以及生石灰混合并将混合物料造球形成球团；步骤三，将所述球团布入燃气熔分炉中加热反应得到硅锰合金。
【技术特征摘要】
1.一种利用贫锰铁矿制备锰硅合金的方法，其特征在于，包含以下步骤：步骤一，将所述贫锰铁矿烘干并破碎；步骤二，将步骤一中破碎后的贫锰铁矿与硅粉以及生石灰混合并将混合物料造球形成球团；步骤三，将所述球团布入燃气熔分炉中加热反应得到硅锰合金。2.根据权利要求1所述的利用贫锰铁矿制备锰硅合金的方法，其特征在于，所述贫锰铁矿中含有以下质量分数的组分：锰为15-20％，铁为28-35％，氧化钙为2-4％，氧化镁为0.5-1％，二氧化硅为13-16％以及三氧化二铝为4-8％。3.根据权利要求1所述的利用贫锰铁矿制备锰硅合金的方法，其特征在于，所述步骤二中贫锰铁矿、硅粉以及生石灰按照质量比100:(18-28):(20-38)进行混合。4.根据权利要求1所述的利用贫锰铁矿制备锰硅合金的方法，其特征在于，所述硅粉为硅灰和/或工业硅粉。5.根据权利要求1所述的利用贫锰铁矿制备锰硅合金的方法，其特征在于，所述燃气熔分炉的温度为1450-1550℃。6.根据权利要求1所述的利用贫锰铁矿制备锰硅合金的方法，其特征在于，所述硅粉...