The invention relates to a small electronic transformer potting, including two components A, B high temperature curing, which is characterized in that: the components of A: bisphenol A epoxy resin, polyether 14%, 52%, 2%, 30% aluminum coupling agent, leveling agent, pigment 1% 1%; B group: two MTHPA, 85% polyester resin 5%, special coupling agent 5%, defoaming agent 1%, DMP30 4%. The preparation method of the invention is simple, low energy consumption, short production cycle, low production cost, stable product performance, for more than 2 hours of the product after mixing, high temperature and short curing time, bright appearance, high performance PPT/PPO adhesive, anti cracking, high electrical performance, high temperature reaches 100 degrees celsius.
【技术实现步骤摘要】
一种小型电子变压器灌封胶
本专利技术专利属于灌封胶领域,尤其涉及一种小型电子变压器灌封胶。
技术介绍
目前电子变压器灌封以双组份酸酐固化环氧树脂为主,因线圈骨架及外壳以PPT、PPO材质为主,由于材质的特性环氧树脂粘接性能不理想,经常出现开裂、电晕、击穿等问题,各个厂家通过对环氧树脂二次改性来解决上述问题。专利技术专利内容本专利技术专利提供一种小型电子变压器灌封胶,主要解决环氧树脂制成单组份胶后储存时间短,低温固化不完全,粘度大工艺性差,成本高。采用价格较低的普通双酚A型环氧树脂,配合改性咪唑潜伏性固化剂,易混合,储存稳定,固化温度低,对塑料金属粘接性能好,从而提高应用客户的品质,降低客户的生产制造成本,节约能耗。本专利技术专利所解决的技术问题采用以下技术方案来实现:一种小型电子变压器灌封胶,包括双组份A、B高温固化,A组分:双酚A型环氧树脂52%、聚醚多元醇14%、氢氧化铝30%、偶联剂2%、流平剂1%、颜料1%;B组分:二甲基四氢苯酐85%、聚酯树脂5%、专用偶联剂5%、消泡剂1%、DMP30-4%。进一步地,A组分的制作方法为,依次将液体原料加入搪瓷搅拌罐内升温至65℃±5℃搅拌1h,然后加入固体粉料温度保持在65℃±5℃搅拌2h,后降温至50℃±5℃经三联辊研磨后包装。进一步地,B组分的制作方法为,将二甲基事情苯酐加入搪瓷搅拌罐内升温至60℃±5℃,缓慢加入聚酯树脂搅拌1-2h,待温度降至45℃左右加入专用偶联剂、消泡剂、DMP30继续搅拌1h,降温至25℃±5℃,放料包装。进一步地,A、B配比为100:40。本专利技术的有益效果在于:本专利技术制 ...
【技术保护点】
一种小型电子变压器灌封胶,包括双组份A、B高温固化,其特征在于:A组分:双酚A型环氧树脂52%、聚醚多元醇14%、氢氧化铝30%、偶联剂2%、流平剂1%、颜料1%;B组分:二甲基四氢苯酐85%、聚酯树脂5%、专用偶联剂5%、消泡剂1%、DMP30‑4%。
【技术特征摘要】
1.一种小型电子变压器灌封胶,包括双组份A、B高温固化,其特征在于:A组分:双酚A型环氧树脂52%、聚醚多元醇14%、氢氧化铝30%、偶联剂2%、流平剂1%、颜料1%;B组分:二甲基四氢苯酐85%、聚酯树脂5%、专用偶联剂5%、消泡剂1%、DMP30-4%。2.根据权利要求1所述的一种小型电子变压器灌封胶,其特征在于:A组分的制作方法为,依次将液体原料加入搪瓷搅拌罐内升温至65℃±5℃搅拌1h,然后加入固体粉料温度...
【专利技术属性】
技术研发人员:骆良德,
申请(专利权)人:天津滨海津丽电子材料有限公司,
类型:发明
国别省市:天津,12
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。