Reflection across the hot water bag water multicolor paint and preparation method thereof, comprising a base paint and a continuous phase; the base paint comprises filler; the continuous phase including a 5 meter according to the quality 15 modified organic bentonite, 20 25 TiO2 and 70 nm 95 polymer resin; quality the filler and the organic modified bentonite is 1:0.1 1. The invention improves the space structure of water in water multicolor paint by mixing the continuous phase and the base paint according to the predetermined proportion formula, and improves the light reflection ability and the heat preservation capability.
【技术实现步骤摘要】
反射隔热水包水多彩涂料及其制备方法
本专利技术通常涉及涂料领域，具体地涉及反射隔热水包水多彩涂料及其制备方法。
技术介绍
随着“十一五”国家节能减排序幕的拉开，隔热、保温、节能成了经济发展重中之重，特别是高层建筑、仓顶或大面积住宅区要求建筑节能达到65％，所以隔热，保温涂料应运而生。反射隔热外墙涂料能降低暴露于太阳光照射下建筑物的表面温度，减少因太阳辐射向室内热量的传递，这样就大大降低了室内温度节约因空调制冷所消耗的能源。因此，反射隔热保温涂料一经面世备受欢迎。目前，市场上的保温涂料隔热保温储热性能差，含砂反射多彩涂料保温性能差，耐脏污性能差，大多通过改变色漆粒子反射隔热性能达到隔热保温性能，保温效果不能连续。本专利技术通过使用反射隔热乳液使涂料达到保温隔热效果。
技术实现思路
为了解决上述技术问题，本专利技术的专利技术人在深入研究后发现，提供一种具有反射隔热功能的水包水多彩涂料，将连续相和基础漆按照预定比例配方混合，提升水包水多彩涂料的反射和隔热功能。本专利技术的一方面，提供一种反射隔热水包水多彩涂料，其包括基础漆和连续相；其中，所述基础漆包括填料；所述连续相包括按...
【技术保护点】
一种反射隔热水包水多彩涂料，其包括基础漆和连续相；其中，所述基础漆包括填料；所述连续相包括按照质量份计的5‑15份改性有机膨润土、20‑25份纳米TiO2和70‑95份聚合物树脂；所述填料与所述改性有机膨润土的质量比为1:0.1‑1。
【技术特征摘要】
1.一种反射隔热水包水多彩涂料，其包括基础漆和连续相；其中，所述基础漆包括填料；所述连续相包括按照质量份计的5-15份改性有机膨润土、20-25份纳米TiO2和70-95份聚合物树脂；所述填料与所述改性有机膨润土的质量比为1:0.1-1。2.根据权利要求1所述的反射隔热水包水多彩涂料，其中，所述聚合物树脂包括按照质量份计的下述组份：5-10份聚氯乙烯、1-5份环氧硬脂酸丁酯、10-15份聚酰亚胺、20-25份十二碳酯和35-50份丙烯酸酯树脂。3.根据权利要求2所述的反射隔热水包水多彩涂料，其中，所述聚酰亚胺为含有烷基侧链和苯环的聚酰亚胺；其中，所述烷基侧链数为14-16，所述苯环数为14-16。4.根据权利要求1所述的反射隔热水包水多彩涂料，其中，所述连续相还包括LD超疏水性纳米界面剂。5.根据权利要求1所述的反射隔热水包水多彩涂料，其中，所述连续相还包括增稠剂和pH调节剂；所述增稠剂为疏水改性碱溶性乳液型增稠剂；所述pH调节剂为2-氨基-2-甲基-1-丙醇AMP-95、丁基乙醇胺或2-氨基-2-甲基-1-丙醇AMP-95与丁基乙醇胺的混合物。6.根据权利要求1所述的反射隔热水包水多彩涂料，其中，所述基础漆还包括纤维素，所述纤维素为羟乙基纤维素250HBR、羟乙基纤维素HS10W或羟乙基纤维素250HBR和羟乙基纤维素HS10W的混合...
【专利技术属性】
技术研发人员：胡效晶，刘胜普，
申请(专利权)人：河北晨阳工贸集团有限公司，
类型：发明
国别省市：河北,13