The invention discloses a fluorocarbon resin synthesis process, control the cooling time based on (a) include: first, according to a certain proportion of the fluorine containing alkene, allyl ester, acid, allyl ether, epoxy resin, catalyst and initiator reactor; (b) adding solvent to the reaction vessel, mixing (c); adjusting reaction temperature and pH value in certain stirring speed, reaction time; (d) the reaction mixture was distilled at a certain pressure and temperature; (E) the product of the distilled cooling of 2 ~ 4h, then dried, powdered, get the target product. The invention can be successfully synthesized for fluorocarbon resin, and the synthesis of high efficiency, low synthesis cost, performance of the product synthesized; and through the cooling time control in the reaction process, so as to improve the reaction rate and product performance.
【技术实现步骤摘要】
本专利技术涉及一种基于控制冷却时间的氟碳树脂合成工艺。
技术介绍
氟碳树脂以牢固的C-F键为骨架,同其他树脂相比,其耐热性、耐化学品性、耐寒性、低温柔韧性、耐候性和电性能等均较好,且由于其结晶性好,故具有不黏附性、不湿润性。广泛应用于厨房和烹调用具,造型模具,机械滑动部分、食品、纺织、造纸等工业用机械的高级卷材涂料,各种罐类、输送管线、泵类、反应釜、换热器及精密器械等的涂装及衬里方面。由于氟碳树脂均系高熔点(180~380℃),不溶于溶剂的固态树脂,故制成水或溶剂的分散型涂料,用喷涂、静电喷涂、幕式淋涂、辊涂等方式涂装,或作成粉末涂料,用静电喷涂或流化床浸涂法涂装。在合成氟碳树脂的工艺过程中,冷却时间将直接影响到反应转化率和产品性能,如何确定一个适当的冷却时间,对氟碳树脂的合成工艺显得尤为重要。
技术实现思路
本专利技术的目的在于克服上述现有技术的缺点和不足,提供一种基于控制冷却时间的氟碳树脂合成工艺,该工艺能成功合成出用于氟碳树脂,且合成效率高,合成成本低,合成出的产品性能好;且通过控制反应过程中的冷却时间,从而提高了反应转化率和产品性能。本专利技术的目的通过下述技术方案实现:一种基于控制冷却时间的氟碳树脂合成工艺,包括以下步骤:(a)首先,按照一定比例将含氟烯烃、烯酯、烯酸、烯醚、环氧树脂、催化剂和引发剂加入反应器内;(b)向反应容器中加入溶剂,搅拌混合均匀;(c)调节反应体系的温度和pH值,在一定的搅拌速度下,反应一段时间;(d)将反应混合物在一定压力和温度 ...
【技术保护点】
一种基于控制冷却时间的氟碳树脂合成工艺,其特征在于,包括以下步骤:(a)首先,按照一定比例将含氟烯烃、烯酯、烯酸、烯醚、环氧树脂、催化剂和引发剂加入反应器内;(b)向反应容器中加入溶剂,搅拌混合均匀;(c)调节反应体系的温度和pH值,在一定的搅拌速度下,反应一段时间;(d)将反应混合物在一定压力和温度下进行蒸馏;(e)将蒸馏出的产物进行冷却2~4h,然后干燥,磨成粉末状,得到目标产品。
【技术特征摘要】
1.一种基于控制冷却时间的氟碳树脂合成工艺,其特征在于,包括以下步骤:
(a)首先,按照一定比例将含氟烯烃、烯酯、烯酸、烯醚、环氧树脂、催化剂和引发剂加入反应器内;
(b)向反应容器中加入溶剂,搅拌混合均匀;
(c)调节反应体系的温度和pH值,在一定的搅拌速度下,反应一段时间;
(d)将反应混合物在一定压力和温度下进行蒸馏;
(e)将蒸馏出的产物进行冷却2~4h,然后干燥,磨成粉末状,得到目标产品。
2.根据权利要求1所述的一种基于控制冷却时间的...