A kind of high thermal conductivity of wood, which is characterized in that the high thermal conductivity of wood components by weight of a thermoplastic resin composition: 80 100 copies, 110 copies, 100 wood powder 12, 10 compatibilizer modified graphite 5 7 copies, 8 copies, 6 coupling agent CaCO310 15 8, lubricant 12, toughening agent 6 8. The invention adopts the modified graphite materials, improve the interfacial compatibility of graphite and, at the same time enhance the thermal conductivity of wood plastic material, the invention adopts maleic anhydride grafted high density polyethylene as the compatibilizer greatly increased wood powder, resin and other materials of the interface, and then provided high mechanical properties of materials.
【技术实现步骤摘要】
一种高导热木塑及其制备方法
本专利技术涉及木塑材料，尤其涉及一种高导热木塑及其制备方法。
技术介绍
木塑复合材料(woodplasticcomposite，简称“WPC”)是国内外近年蓬勃兴起的一类新型复合材料，该复合材料时利用聚乙烯、聚丙烯和聚氯乙烯等高分子材料，代替通常的树脂胶粘剂，与超过35％—70％以上的木粉、稻壳、秸秆等废植物纤维混合成新的木质材料，再经挤压、模压、注射成型等塑料加工工艺,生产出的板材或型材。木塑复合材料具有很多优良性能，其主要用于建材、家具、装饰等行业。而现在室内装饰、换热工程、采暖工程、电子信息工程等方面往往会采用高导热材料。然而，绝大数高分子材料热导率极低，是热的不良导体，必须要添加导热系数较高的填充材料来提高木塑材料的导热性能。
技术实现思路
本专利技术的目的是一种高导热木塑及其加工方法，该高导热木塑以木粉和混合树脂为主要原料，辅以各种助剂，制备所得的复合材料导热性能高，力学性能优越。本专利技术解决技术问题采用如下技术方案：一种高导热木塑，其特征在于，所述高导热木塑组份按重量份组成为：热塑性树脂80-100份、木粉100-110份、相...
【技术保护点】
一种高导热木塑，其特征在于，所述高导热木塑组份按重量份组成为：热塑性树脂80‑100份、木粉100‑110份、相容剂10‑12份、改性石墨5‑7份、偶联剂6‑8份、CaCO310‑15份、润滑剂8‑12份、增韧剂6‑8份。
【技术特征摘要】
1.一种高导热木塑，其特征在于，所述高导热木塑组份按重量份组成为：热塑性树脂80-100份、木粉100-110份、相容剂10-12份、改性石墨5-7份、偶联剂6-8份、CaCO310-15份、润滑剂8-12份、增韧剂6-8份。2.根据权利要求1所述的一种高导热木塑，其特征在于，所述热塑性树脂为HDPE。3.根据权利要求1所述的一种高导热木塑，其特征在于，所述HDPE树脂熔融指数为0.25g/10min。4.根据权利要求1所述的一种高导热木塑，其特征在于，所述相容剂为马来酸酐接枝高密度聚乙稀。5.一种高导热木塑的制备方法，其特征在于，按如下...
【专利技术属性】
技术研发人员：方晓钟，肖磊，马岩，姚红焱，高威威，贾红滢，徐民，
申请(专利权)人：安徽国风木塑科技有限公司，
类型：发明
国别省市：安徽,34