The invention discloses a preparation method of PVC leather with nanometer straw carbon black, PVC calendering leather and a nanometer straw carbon black. The straw carbon containing nano PVC calendaring leather including PVC resin, straw ash, plasticizer and nano carbon black straw, the components according to the mass ratio for PVC resin 100, straw ash 40 95 copies, 100 copies of 20 plasticizer, stabilizer 1 4, 2 15 nano carbon black straw a. Instead of black cake, nano straw carbon black is used to avoid non renewable resources such as oil and natural gas. As a renewable resource, nano straw carbon black can effectively increase the added value of straw.
【技术实现步骤摘要】
含纳米秸秆炭黑PVC压延革及其制备方法
本专利技术属于压延革
，具体涉及一种含纳米秸秆炭黑PVC压延革和一种含纳米秸秆炭黑PVC压延革制备方法。
技术介绍
据统计，我国每年产生约9亿吨农作物秸秆，其中约20%-40%的秸秆通过燃烧方式进行处理，另有小部分秸秆作为钾肥来还田之外，还有相当比例的秸秆无法有效处理。上述秸秆处理方式不仅商业经济效益低，而且产生大量粉尘，严重污染环境。秸秆燃烧过程中产生大量秸秆灰。随着公众对空气质量，特别是PM2.5指数的重视程度不断提高，如何环保并且高效地利用秸秆灰成为热门的探索方向之一。传统黑色PVC压延革中，用黑色色饼作为颜色对PVC压延革进行调色。生产黑色色饼所用的炭黑大多采用石油裂解后的液态烃，或者天然气为主要原料，经过不完全燃烧或热解获得。石油和天然气均为不可再生资源，而纳米秸秆炭黑是利用生物质秸秆为原料经特殊工艺制备的纳米黑色粉末，是一种资源可再生产品，且可将秸秆变废为宝，提高其附加值。为此，有必要提出一种新型PVC压延革。在同等条件下,将纳米秸秆炭黑代替黑色色饼，具有较高的经济效益和环保价值。
技术实现思路
本专利技术针对...
【技术保护点】
一种含纳米秸秆炭黑PVC压延革，其特征在于，包括PVC树脂、秸秆灰、增塑剂和纳米秸秆炭黑，上述各组分按质量配比计为：PVC树脂 100份；秸秆灰 40‑95份；增塑剂 20‑100份；稳定剂 1‑4份；纳米秸秆炭黑 2‑15份。
【技术特征摘要】
1.一种含纳米秸秆炭黑PVC压延革，其特征在于，包括PVC树脂、秸秆灰、增塑剂和纳米秸秆炭黑，上述各组分按质量配比计为：PVC树脂100份；秸秆灰40-95份；增塑剂20-100份；稳定剂1-4份；纳米秸秆炭黑2-15份。2.根据权利要求1所述的含纳米秸秆炭黑PVC压延革，其特征在于，上述PVC树脂为3型、5型树脂中的一种或两者的混合物。3.根据权利要求1所述的含纳米秸秆炭黑PVC压延革，其特征在于，上述秸秆灰为稻草秸秆灰、小麦秸秆灰、玉米秸秆灰、大豆秸秆灰中的一种或几种的混合物。4.根据权利要求1所述的含纳米秸秆炭黑PVC压延革，其特征在于，上述增塑剂为邻苯二甲酸二辛酯、邻苯二甲酸二丁酯、邻苯二甲酸二(2-乙基己)酯、邻苯二甲酸二(2-丙基庚)酯中的一种或几种混合物。5.根据权利要求1所述的含纳米秸秆炭黑PVC压延革，其特征在于，上述稳定剂为钙锌复合稳定剂、钡锌复合稳定剂、液体复合稳定剂中的一种或几种的混合物。6.一种含纳米秸秆炭黑PVC压延革制备方法，其特征在于，包括以下步骤：步骤S1：按质量配比...
【专利技术属性】
技术研发人员：张惠良，江雄知，
申请(专利权)人：嘉兴市博尔塑胶有限公司，
类型：发明
国别省市：浙江,33