The present invention discloses environment-friendly plastic can be rapidly degraded, which comprises the following components: 45 weight fraction 50 starch, 40 45 copies, 0.05 copies of 0.03 polyethylene hydrolase, 0.015 0.15 copies, 1.5 copies of 1 crosslinking esterification agent, 1.5 2.5 copies, 1 copies of 0.5 flexible agent light 0.5 1 copies of degrading agent, light stabilizer, 0.5 1 lubricants, ethylene vinyl alcohol copolymer 5 10 copies, 5 copies of 3 pentaerythritol. The invention adopts the synthesis of starch and polyethylene plastic, the plastic biodegradable; and the invention uses light degradation and biodegradation, improve the degradation rate of plastic; the hydrolysis of starch in plastics and polyethylene and reinforced thermoplastic starch, for plastics recycling.
【技术实现步骤摘要】
可快速降解的环保型塑料
本专利技术涉及一种可降解塑料，具体涉及可快速降解的环保型塑料。
技术介绍
塑料是以单体为原料，通过加聚或缩聚反应聚合而成的高分子化合物，俗称塑料或树脂，可以自由改变成分及形体样式，由合成树脂及填料、增塑剂、稳定剂、润滑剂、色料等添加剂组成。塑料的主要成分是树脂，树脂是指尚未和各种添加剂混合的高分子化合物，树脂约占塑料总重量的40％～100％。塑料的基本性能主要决定于树脂的本性，但添加剂也起着重要作用。有些塑料基本上是由合成树脂所组成，不含或少含添加剂，如有机玻璃、聚苯乙烯等。塑料是重要的有机合成高分子材料，应用非常广泛。但是废弃塑料带来的"白色污染"也越来越严重，塑料容易燃烧，燃烧时产生有毒气体。例如聚苯乙烯燃烧时产生甲苯，这种物质少量会导致失明，吸入有呕吐等症状，PVC燃烧也会产生氯化氢有毒气体，除了燃烧，就是高温环境，会导致塑料分解出有毒成分，例如苯等；并且塑料在土壤中完全被微生物同化，降解成CO2和水实现无机矿化，可能需要200-400年时间，从而造成在环境中的积累，由于塑料的无法降解及降解速度慢，塑料污染已成为重要污染之一。专利技术...
【技术保护点】
可快速降解的环保型塑料，其特征在于，包括以下重量分数的组分：45‑50份淀粉、40‑45份聚乙烯、0.03‑0.05份水解酶、0.015‑0.15份交联剂、1‑1.5份酯化剂、1.5‑2.5份柔性剂、0.5‑1份光降解剂、0.5‑1份光稳定剂、0.5‑1份润滑剂、乙烯‑乙烯醇共聚物5‑10份、季戊四醇3‑5份。
【技术特征摘要】
1.可快速降解的环保型塑料，其特征在于，包括以下重量分数的组分：45-50份淀粉、40-45份聚乙烯、0.03-0.05份水解酶、0.015-0.15份交联剂、1-1.5份酯化剂、1.5-2.5份柔性剂、0.5-1份光降解剂、0.5-1份光稳定剂、0.5-1份润滑剂、乙烯-乙烯醇共聚物5-10份、季戊四醇3-5份。2.根据权利要求1所述的可快速降解的环保型塑料，其特征在于，还包括以下重量分数的组分：0.5-1份酒石酸、球形二氧化硅1-2份。3.根据权利要求2所述的可快速降解的环保型塑料，其特征在于，所述光降解剂采用二硫代氨基甲酸...
【专利技术属性】
技术研发人员：曾建华，
申请(专利权)人：四川索朗臣环保科技有限公司，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。