本发明专利技术属于高分子材料技术领域，具体提供了一种抗老化ABS色母粒，由如下重量份数的组分组成：PE载体100~120份；色粉2~20份；表面处理剂5～10份；分散剂3~8份；热稳定剂0.5~3份；塑料抗老化剂0.1~10份。本发明专利技术抗老化效果好、寿命长，制作工艺简单，易于操作，生产成本低，对环境污染较小，有较广阔的应用前景，解决了现有色母粒热稳定性差造成的颜色不稳定、色差不易控制等问题。

An anti aging ABS Masterbatch

The invention belongs to the technical field of polymer materials, especially a kind of anti aging ABS masterbatch, by weight of the following components: PE vector 100~120; 2~20 toner; surface treatment agent 5 ~ 10; dispersant 3~8; heat stabilizer 0.5~3; plastic anti aging agent 0.1 ~10 copies. The invention of anti aging effect, long service life, simple manufacturing process, easy operation, low production cost, less environmental pollution, and it has broad application prospects, solves the problem of poor heat stability of existing Masterbatch color is not stable, the color is not easy to control etc..

【技术实现步骤摘要】
一种抗老化ABS色母粒
本专利技术属于高分子材料
，具体涉及一种抗老化ABS色母粒。
技术介绍
色母料是由树脂和大量颜料(达50%)或染料配制成高浓度颜色的混合物。色母又名色种，是一种把超常量的颜料或染料均匀载附于树脂之中而制得的聚集体。企业加工时用少量色母料和未着色树脂掺混，就可达到设计颜料浓度的着色树脂，由于它具有优异的机械强度、电绝缘性、耐热性和耐化学品性，因而它主要应用于合成纤维、电器绝缘材料和胶片等领。但是随着色母粒广泛的应用，对色母粒也提出更好的要求，在成型加工时由于色母粒热稳定性差容易造成颜色不稳定、色差不易控制等问题。
技术实现思路
本专利技术的目的是克服现有技术的缺陷，提供一种提高颜色的均匀性和稳定性，抗老化效果较好，可降低生产成本低的抗老化ABS色母粒。为此，本专利技术提供了一种抗老化ABS色母粒，由如下重量份数的组分组成：PE载体100~120份；色粉2~20份；表面处理剂5～10份；分散剂3~8份；热稳定剂0.5~3份；塑料抗老化剂0.1~10份。作为优选，由如下重量份数的组分组成：PE载体100份；色粉2份；表面处理剂5份；分散剂3份；热稳定剂0.5份；塑本文档来自技高网...

【技术保护点】
一种抗老化ABS色母粒，其特征在于：由如下重量份数的组分组成：PE载体100 ~ 120份；色粉2 ~ 20份；表面处理剂5～10份；分散剂3 ~ 8份；热稳定剂0 .5 ~ 3份；塑料抗老化剂0.1 ~ 10份。

【技术特征摘要】
1.一种抗老化ABS色母粒，其特征在于：由如下重量份数的组分组成：PE载体100~120份；色粉2~20份；表面处理剂5～10份；分散剂3~8份；热稳定剂0.5~3份；塑料抗老化剂0.1~10份。2.如权利要求1所述的一种抗老化ABS色母粒，其特征在于，由如下重量份数的组分组成：PE载体100份；色粉2份；表面处理剂5份；分散剂3份；热稳定剂0.5份；塑料抗老化剂0.1份。3.如权利要求1所述的一种抗老化ABS色母粒，其特征在于，由如下重量份数的组分组成：...