The present invention relates to an antibacterial coating of carbon nanotubes ZnO silver, including a ZnO carbon nanotube supported silver antibacterial agent and paint, wherein, ZnO carbon nanotubes carrying silver antibacterial agent for the Ag load in ZnO carbon nanotubes, antibacterial agent, the total weight of ZnO carbon nanotubes silver ZnO carbon nanotube supported silver antibacterial coating, 0.1 of the total weight of 3%. Nano composite antibacterial agent combines the advantages of nano silver and nano Zinc Oxide, and the antibacterial effect is safer, more stable and more efficient. The invention also provides a preparation method of ZnO carbon nanotubes silver antibacterial agent.
【技术实现步骤摘要】
一种ZnO-碳纳米管载银抗菌涂料及其制备方法
本专利技术涉及涂料领域，具体的涉及一种ZnO-碳纳米管载银抗菌涂料及其制备方法。
技术介绍
抑菌材料是指自身具有杀灭或抑制细菌作用的一类功能材料，银作为新型抑菌材料，因具有杀菌能力强、活性高和渗透性强等优点而被广泛应用。然而，常见块状Ag的抑菌效率低，理论上纳米Ag粒子半径越小，比表面积越大，抑菌效率越高。但纳米Ag在介质中易团聚，降低了纳米Ag的抑菌效率。中国专利申请CN105838164A公开了一种水性纳米抗菌吸音涂料及其制备方法，以重量百分比计，该涂料包括：22～32％丙烯酸树脂乳液、0.5～2％水性纳米银抗菌剂、5～12钛白粉、15～22％填料、10～15膨胀珍珠岩、助剂3.065～7.75％，水18～30％。该专利技术专利所含抗菌活性成份为水性纳米银抗菌剂，抗菌成分单一，不如复合抗菌剂的效果好。
技术实现思路
本专利技术根据现有技术的不足，提供了一种ZnO-碳纳米管载银抗菌涂料及其制备方法。一种ZnO-碳纳米管载银抗菌涂料，包括ZnO-碳纳米管载银抗菌剂和油漆。所述ZnO-碳纳米管载银抗菌剂总重量为ZnO-碳纳米...
【技术保护点】
一种ZnO‑碳纳米管载银抗菌涂料，其特征在于，包括ZnO‑碳纳米管载银抗菌剂和油漆；所述ZnO‑碳纳米管载银抗菌剂总重量为ZnO‑碳纳米管载银抗菌涂料总重量的0.1‑3％；所述ZnO‑碳纳米管载银抗菌剂含有ZnO‑碳纳米管和Ag；所述Ag负载在ZnO‑碳纳米管上；所述碳纳米管为多壁碳纳米管，长15‑25μm，直径50‑75nm；所述ZnO‑碳纳米管载银抗菌剂的制备方法，包括如下步骤：(1)取1.1‑1.5g乙酸锌溶解在200‑250mL一缩二乙二醇中，加入15mL蒸馏水，搅拌并缓慢升温至180℃，继续搅拌5‑10min，取出烧杯静置2‑5h，加入0.1‑1g碳纳米管，超声分...
【技术特征摘要】
1.一种ZnO-碳纳米管载银抗菌涂料，其特征在于，包括ZnO-碳纳米管载银抗菌剂和油漆；所述ZnO-碳纳米管载银抗菌剂总重量为ZnO-碳纳米管载银抗菌涂料总重量的0.1-3％；所述ZnO-碳纳米管载银抗菌剂含有ZnO-碳纳米管和Ag；所述Ag负载在ZnO-碳纳米管上；所述碳纳米管为多壁碳纳米管，长15-25μm，直径50-75nm；所述ZnO-碳纳米管载银抗菌剂的制备方法，包括如下步骤：(1)取1.1-1.5g乙酸锌溶解在200-250mL一缩二乙二醇中，加入15mL蒸馏水，搅拌并缓慢升温至180℃，继续搅拌5-10min，取出烧杯静置2-5h，加入0.1-1g碳纳米管，超声分散1-2h，缓慢加热至180℃，搅拌1-2...