The invention discloses a filler containing neutral pale green wax model, according to the weight percentage is composed of the following components: according to weight ratio, which is composed of the following components: 1, 5% ~ 10% of paraffin wax and microcrystalline wax 5% ~ 15%, 10% ~ 20%, as well as 15% stearic acid resin 5% ~ ~ 20%, 10%, 11% ~ 20% ethylene copolymer, polymer filler was 30% ~ 40%, the casting wax quality and 100% percentage points. The product is a neutral filler containing pale green wax wax model, has a wide range of high-grade large mould wax wax model without cavitation. It has excellent surface finish, moderate hardness, dimensional stability, and very good fluidity. It is widely used, and the blade of a propeller with ceramic core is very suitable for general super large castings and thin shell castings. Since it is a very low residual wax filling wax, it is suitable for general iron casting and alloy casting.
【技术实现步骤摘要】
一种含有中性填料的淡绿色模型蜡
本专利技术涉及一种模型蜡及制备工艺，特别涉及一种含有中性填料的淡绿色模型蜡。
技术介绍
随着中国经济领域的深化改革，制造业得到了长足的发展，作为制造业一项关键技术，精密铸造产品在中国的各个工业领域得到了更广泛的应用。而精密铸造蜡恰恰是精密铸造过程中必不可缺的关键环节产品。在中国市场每年大约需要2万吨的精密铸造蜡，以前高端精密铸造蜡完全需要进口，我公司的这款产品具有国外产品相同的性能，市场应用前景非常广泛。
技术实现思路
本专利技术要解决的技术问题是克服现有技术的缺陷，提供一种含有中性填料的淡绿色模型蜡及制备工艺。为了解决上述技术问题，本专利技术提供了如下的技术方案：本专利技术一种含有中性填料的淡绿色模型蜡，按重量百分比计由下列组分组成：按重量比计由下列组分组成：1、石蜡类5%～10%、微晶蜡5%～15%,地蜡10%～20%、硬脂酸15%～20%、树脂类5%～10%、乙烯共聚物类11%～20%,高分子填充物30%～40%、所述铸造蜡的各组分质量百分比之和为100%。作为本专利技术的一种优选技术方案，该制备工艺是按上述配比首先：将蜡料放入压...
【技术保护点】
一种含有中性填料的淡绿色模型蜡，其特征在于，按重量百分比计由下列组分组成：按重量比计由下列组分组成：1、石蜡类5%～10%、微晶蜡5%～15%,地蜡10%～20%、硬脂酸15%～20%、树脂类5%～10%、乙烯共聚物类11%～20%,高分子填充物30%～40%、所述铸造蜡的各组分质量百分比之和为100%。
【技术特征摘要】
1.一种含有中性填料的淡绿色模型蜡，其特征在于，按重量百分比计由下列组分组成：按重量比计由下列组分组成：1、石蜡类5%～10%、微晶蜡5%～15%,地蜡10%～20%、硬脂酸15%～20%、树脂类5%～10%、乙烯共聚物类11%～20%,高分子填充物30%～40%、所述铸造蜡的各组分质量百分比之和为100%。2.一种含有中性填料的淡绿色模型蜡的制备工艺，其特征在于，该制备工艺是按上述配比首...
【专利技术属性】
技术研发人员：李斌，
申请(专利权)人：上海宜祥石油化工科技有限公司，
类型：发明
国别省市：上海,31