The invention discloses a special TPE materials coated nylon with glass fibre and its preparation method, the raw materials by weight are as follows: styrene thermoplastic elastomer 20 30, white 30 40 copies, 15 copies of the 5 polyolefin, polyolefin elastomer 5 10 copies, 25 compatibilizer 30 copies, 10 copies of 0 filler. A special TPE material coated nylon with glass fibre and its preparation method of the invention, the compatibility of high concentration agent in polar components and nylon with glass fibre surface plastic in high temperature double material forming good binding, solve the difference easily binding force of traditional TPE material plastic bags nylon with glass fiber problems when added TPE material use and commercial value.
【技术实现步骤摘要】
一种专于包胶尼龙加玻纤的TPE材料及其制备方法
本专利技术涉及TPE材料
，尤其涉及一种专于包胶尼龙加玻纤的TPE材料及其制备方法。
技术介绍
用于包胶尼龙(PA6，PA66)加玻纤的TPE(热塑性弹性体)的配方通常是由苯乙烯类热塑性弹性体(SEBS)、白油、相容剂和TPU(热塑性聚氨酯弹性体)等原材料组成的共混物，此类TPE共混材料在用于与ABS、PC等极性材料双物料共塑(即包胶)时的粘接效果很好，但在用于包胶PA6或PA66加玻纤时的粘接效果很差，容易剥落，所以限制了TPE材料在包胶尼龙加玻纤时的应用。TPE材料在包胶尼龙加玻纤时的应用解决是我们需要面对的问题。
技术实现思路
本专利技术的目的是为了解决现有技术中存在的缺点，而提出的一种专于包胶尼龙加玻纤的TPE材料及其制备方法。为了实现上述目的，本专利技术采用了如下技术方案：一种专于包胶尼龙加玻纤的TPE材料，其原料按重量份如下：苯乙烯类热塑性弹性体20-30份，白油30-40份，聚烯烃5-15份，聚烯烃弹性体5-10份，相容剂25-30份，填料0-10份。优选的，所述填料为矿物质填料。优选的，所述相容剂为...
【技术保护点】
一种专于包胶尼龙加玻纤的TPE材料及其制备方法，其特征在于：其原料按重量份如下：苯乙烯类热塑性弹性体20‑30份，白油30‑40份，聚烯烃5‑15份，聚烯烃弹性体5‑10份，相容剂25‑30份，填料0‑10份。
【技术特征摘要】
1.一种专于包胶尼龙加玻纤的TPE材料及其制备方法，其特征在于：其原料按重量份如下：苯乙烯类热塑性弹性体20-30份，白油30-40份，聚烯烃5-15份，聚烯烃弹性体5-10份，相容剂25-30份，填料0-10份。2.根据权利要求1所述的一种专于包胶尼龙加玻纤的TPE材料，其特征在于：所述填料为矿物质填料。3.根据权利要求1所述的一种专于包胶尼龙加玻纤的TPE材料，其特征在于：所述相容剂为聚烯烃接枝马来酸酐。4.一种权利要求1所述的专于包胶尼龙加玻纤的TPE材料的制备方法，其特征在于：包...