The invention discloses a fireproof glass coating and a preparation method thereof, 50 100 glass fiber into 50 100 deionized water, stirring evenly; the solution to add 1 5 carbon forming agent, 1 3 1 5 advection agent, cross-linking agent and 1 5 gel, 60 at 80 DEG C, stirring at 1000 2000r/min speed for at least 40 minutes, glass fire coating semi-finished products; add 1 to the glass fire glue in semi-finished products 3 defoaming agent, stirring at 5000 6000r/min speed for at least 20 minutes, fire glass coating products. The preparation of the invention is simple and easy to obtain, the manufacturing process is simple and easy to operate; the finished product is coated on the glass, and the transmission property of the glass is not affected, and the fireproof performance of the glass is enhanced.
【技术实现步骤摘要】
一种玻璃防火涂胶及其制备方法
本专利技术涉及一种涂胶，具体涉及一种玻璃防火涂胶及其制备方法。
技术介绍
玻璃是一种透明、强度及硬度颇高，不透气的物料，被广泛用于各种建筑上。然而，普通玻璃不具备防火功能，特种防火玻璃虽具有控制火势蔓延、隔烟和隔热等性能，但其制作工艺复杂、成本较高。为了火灾发生时给有效救护提供了宝贵的救援时间，最大限度地降低了人员、财产和建筑物的损失，需要采取积极措施，提升现有普通玻璃的防火性能。
技术实现思路
解决的技术问题：针对现有技术的不足，本专利技术提供了一种玻璃防火涂胶及其制备方法，提高现有玻璃的防火性能。技术方案：本专利技术提供的一种玻璃防火涂胶，由以下重量份数的原料制成：玻璃纤维50-100份、去离子水50-100份、成炭剂1-5份、平流剂1-3份、交联剂1-5份、凝胶剂1-5份、消泡剂1-3份。所述成炭剂为果糖、葡萄糖中的一种或两者的混合物，两者混合使用时质量比为1:(1-1.5)。所述平流剂为二丙酮醇。所述交联剂为氟硅酸钠、氟硅酸钾中的一种或两者的混合物，两者混合使用时质量比为1:(1-1.5)。所述凝胶剂为聚丙烯酸、海藻酸中的一种或两...
【技术保护点】
一种玻璃防火涂胶，其特征在于由以下重量份数的原料制成：玻璃纤维50‑100份、去离子水50‑100份、成炭剂1‑5份、平流剂1‑3份、交联剂1‑5份、凝胶剂1‑5份、消泡剂1‑3份。
【技术特征摘要】
1.一种玻璃防火涂胶，其特征在于由以下重量份数的原料制成：玻璃纤维50-100份、去离子水50-100份、成炭剂1-5份、平流剂1-3份、交联剂1-5份、凝胶剂1-5份、消泡剂1-3份。2.根据权利要求1所述的一种玻璃防火涂胶，其特征在于：所述成炭剂为果糖、葡萄糖中的一种或两者的混合物，两者混合使用时质量比为1:(1-1.5)。3.根据权利要求1所述的一种玻璃防火涂胶，其特征在于：所述平流剂为二丙酮醇。4.根据权利要求1所述的一种玻璃防火涂胶，其特征在于：所述交联剂为氟硅酸钠、氟硅酸钾中的一种或两者的混合物，两者混合使用时质量比为1:(1-1.5)。5.根据权利要求1所述的一种玻璃防火涂胶，其特征在于：所述凝胶剂为聚丙...
【专利技术属性】
技术研发人员：苏复，孙祯彬，赵庆，孙俊，佟鹏飞，
申请(专利权)人：句容耀皮节能玻璃科技发展有限公司，
类型：发明
国别省市：江苏,32