The invention discloses an environment-friendly galvanized liquid and a preparation method thereof, wherein the preparation method comprises the following steps: zinc chloride, ammonium chloride, potassium chloride, sodium hydroxide, triethanolamine, brightener and water mixing, heating and stirring and adding zinc powder, the environmental protection to solve the traditional galvanizing liquid bath with copper and nickel and chromium metal plating solution, these heavy metals not only cause a lot of pollution, while the production of wastewater generated in the process is also very difficult to deal with, after the completion of the coating coating was the problem of poor ability.
【技术实现步骤摘要】
一种环保镀锌液及其制备方法
本专利技术涉及电镀液，特别涉及一种环保镀锌液及其制备方法。
技术介绍
为了进一步提高某些特定加工件的钝化能力、良好的化学稳定性以及发光能力，进一步满足加工件的美观效果和防护目的，会在加工件的外表面镀上镀层，传统镀液采用铜、镍及铬类的金属镀液，这些重金属不仅会产生很大的污染，同时生产过程中产生的废水也很难处理，镀膜完成后的镀层耐磨能力较差。
技术实现思路
本专利技术所要解决的技术问题是提供一种环保镀锌液及其制备方法，解决了传统镀液采用铜、镍及铬类的金属镀液，这些重金属不仅会产生很大的污染，同时生产过程中产生的废水也很难处理，镀膜完成后的镀层耐磨能力较差的问题。为实现上述目的，本专利技术提供以下的技术方案：一种环保镀锌液的制备方法，其中，所述制备方法包括：将氯化锌、氯化铵、氯化钾、氢氧化钠、三乙醇胺、光亮剂和水混合，加热搅拌并加入锌粉，得到所述环保镀锌液，其中，相对于100重量份的氯化锌，所述氯化铵的用量为20-40重量份，所述氯化钾的用量为10-20重量份，所述氢氧化钠的用量为5-15重量份，所述三乙醇胺的用量为25-45重量份，所述光亮剂的...
【技术保护点】
一种环保镀锌液的制备方法，其特征在于，所述制备方法包括：将氯化锌、氯化铵、氯化钾、氢氧化钠、三乙醇胺、光亮剂和水混合，加热搅拌并加入锌粉，得到所述环保镀锌液，其中，相对于100重量份的氯化锌，所述氯化铵的用量为20‑40重量份，所述氯化钾的用量为10‑20重量份，所述氢氧化钠的用量为5‑15重量份，所述三乙醇胺的用量为25‑45重量份，所述光亮剂的用量为5‑10重量份，所述水的用量为50‑60重量份，所述锌粉的用量为5‑10重量份。
【技术特征摘要】
1.一种环保镀锌液的制备方法，其特征在于，所述制备方法包括：将氯化锌、氯化铵、氯化钾、氢氧化钠、三乙醇胺、光亮剂和水混合，加热搅拌并加入锌粉，得到所述环保镀锌液，其中，相对于100重量份的氯化锌，所述氯化铵的用量为20-40重量份，所述氯化钾的用量为10-20重量份，所述氢氧化钠的用量为5-15重量份，所述三乙醇胺的用量为25-45重量份，所述光亮剂的用量为5-10重量份，所述水的用量为50-60重量份，所述锌粉的用量为5-10重量份。2.根据权利要求1所述的制备方法，其中，相对于100重量份的氯化锌，所述氯化铵的用量为25-35重量份，所述氯化钾的用量为12-18重量份，所述氢氧化钠的用量为8-12重量份，所述三乙醇胺的用量为30-40重量份，...
【专利技术属性】
技术研发人员：张玉，
申请(专利权)人：合肥信亚达智能科技有限公司，
类型：发明
国别省市：安徽,34