The invention discloses a production process of insulating aluminum windows and doors on the basis of the components are evenly mixed according to the proportion of mixing pressed compacts; blank pressed well placed in a vacuum furnace cavity, with 35 50 DEG /min heating rate is heated to 1250 DEG C, holding 5 6h; control of furnace the temperature is 500 DEG C 550, will be placed in the 700 block at a temperature of 750 DEG C for heat treatment of 7 9 hours; the blank by quenching, the quenching temperature is 500 550 DEG C, after quenching temperature control in 250 300 DEG C; after air cooling, reheating after hot rolling; stretching and straightening the tensile, volume control in 1 ~ 2%; aging, the aging temperature is 200 to 220 DEG C, the holding time is 11 12h.
【技术实现步骤摘要】
基于门窗的保温铝材的制作工艺
本专利技术涉及一种铝材，具体涉及基于门窗的保温铝材的制作工艺。
技术介绍
随着科技的发展，合金材料越来越多的被用在门窗的型材上，钛合金、铝合金等均可作为门窗的型材，尤其是铝合金材料，由于铝合金具有轻质、以加工的优点，门窗用铝合金越来越多。然而目前的铝合金隔音效果差，极易变形，在低温条件下韧性下降，很容易断裂，并且不具有较好的保温的作用。
技术实现思路
本专利技术所要解决的技术问题是现有的铝材隔音效果差易变性并且不具有保温作用，并且制备工艺复杂，目的在于提供基于门窗的保温铝材的制作工艺，解决现有的铝材隔音效果差易变性并且不具有保温作用，并且制备工艺复杂的问题。本专利技术通过下述技术方案实现：基于门窗的保温铝材的制作工艺，包括以下步骤：(1)将各组分按比例均匀混合，混合均匀后压制成坯块；(2)将压制好的坯块放置于真空炉腔中，以35-50℃/min的升温速度升温至1250℃，保温5-6h；(3)控制炉内温度为500-550℃，将坯块放置在700-750℃环境下进行热处理7-9小时；(4)将坯块进行淬火处理，淬火温度为500-550℃，淬火后温度...
【技术保护点】
基于门窗的保温铝材的制作工艺，其特征在于，包括以下步骤：(1)将各组分按比例均匀混合，混合均匀后压制成坯块；(2)将压制好的坯块放置于真空炉腔中，以35‑50℃/min的升温速度升温至1250℃，保温5‑6h；(3)控制炉内温度为500‑550℃，将坯块放置在700‑750℃环境下进行热处理7‑9小时；(4)将坯块进行淬火处理，淬火温度为500‑550℃，淬火后温度控制在250‑300℃；(5)空冷后，再加热后进行热轧；(6)拉伸矫直，拉伸量控制在1～2％；(7)时效处理，时效温度为200～220℃，保温时间为11‑12h。
【技术特征摘要】
1.基于门窗的保温铝材的制作工艺，其特征在于，包括以下步骤：(1)将各组分按比例均匀混合，混合均匀后压制成坯块；(2)将压制好的坯块放置于真空炉腔中，以35-50℃/min的升温速度升温至1250℃，保温5-6h；(3)控制炉内温度为500-550℃，将坯块放置在700-750℃环境下进行热处理7-9小时；(4)将坯块进行淬火处理，淬火温度为500-550℃，淬火后温度控制在250-300℃；(5)空冷后，再加热后进行热轧；(6)拉伸矫直，拉伸量控制在1～2％；(7)时效处理，时效温度为200～220℃，保温时间为...
【专利技术属性】
技术研发人员：谢本长，
申请(专利权)人：四川爱斯兰特门窗科技有限公司，
类型：发明
国别省市：四川,51