The present invention provides a method for manufacturing the orthosis, the orthosis of shape memory polymer materials; manufacturing method of shape memory polymer wherein comprises the following steps: acrylate monomer, polyol acrylate and catalyst mixing and crosslinking reaction, thereby generating a shape memory polymer material; wherein, acrylate monomer 50 150 weight portions; polyol acrylate 10 30 weight; 0.01 to 0.2 parts by weight of catalyst. The invention adopts the shape memory polymer temperature sensitive to produce the orthosis, orthosis can be softened at a specific temperature, then be shaped into a new shape, if new shapes are not suitable, also can return to the initial shape orthosis, this reduces due to heavy waste of resources for preparation of orthosis.
【技术实现步骤摘要】
矫形器、用于该矫形器的形状记忆高分子材料的制造方法
本专利技术涉及形状记忆材料领域，尤其涉及一种矫形器、用于该矫形器的形状记忆高分子材料的制造方法；本专利技术的形状记忆高分子材料为聚丙烯酸酯类形状记忆高分子材料。
技术介绍
历经半个多世纪，形状记忆材料已被广为知晓。其中，温度感应型形状记忆聚合物尤为引人关注，这是由它们的高应变恢复能力(最高达800％)引起的，这种温度感应型形状记忆聚合物的应变恢复能力远大于形状记忆合金所能达到的低于8％的最高应变恢复能力。除了具有很高的应变恢复能力外，形状记忆聚合物相对于形状记忆合金还具有重量轻、加工性优越和成本低的优点。对于形状记忆聚合物，必须具有固定相和可逆相。其中，固定相负责记忆聚合物的初始形状并由化学交联或物理交联(例如链缠结和结晶)实现；可逆相决定聚合物新形状的固定和变化，该聚合物的初始形状向新形状的转变可以在玻璃化转变温度或熔化温度时通过外力实现。因为大多数聚合物具有玻璃化转变温度(Tg)、熔化温度(Tm)或上述两种温度，所以这些聚合物可以通过引入交联机制(例如化学交联)转变成形状记忆聚合物。通过所发现形状记忆聚合物的...
【技术保护点】
一种用于矫形器的形状记忆高分子材料的制造方法，其特征在于，包括以下步骤：将丙烯酸酯类单体、多元醇丙烯酸酯类和催化剂混合并发生交联反应，从而生成形状记忆高分子材料；其中，丙烯酸酯类单体50‑150重量份；多元醇丙烯酸酯类10‑30重量份；催化剂0.01‑0.2重量份。
【技术特征摘要】
1.一种用于矫形器的形状记忆高分子材料的制造方法，其特征在于，包括以下步骤：将丙烯酸酯类单体、多元醇丙烯酸酯类和催化剂混合并发生交联反应，从而生成形状记忆高分子材料；其中，丙烯酸酯类单体50-150重量份；多元醇丙烯酸酯类10-30重量份；催化剂0.01-0.2重量份。2.根据权利要求1所述的形状记忆高分子材料的制造方法，其特征在于，丙烯酸酯类单体包括甲基丙烯酸甲酯、甲基丙烯酸乙酯、甲基丙烯酸丙酯以及甲基丙烯酸丁酯中的一种或多种。3.根据权利要求1所述的形状记忆高分子材料的制造方...
【专利技术属性】
技术研发人员：胡金莲，陈诚，
申请(专利权)人：香港纺织及成衣研发中心有限公司，
类型：发明
国别省市：中国香港,81