The invention relates to a waterproof coating, including cement, active masterbatch, acrylic resin, epoxy resin, pigments and fillers, adhesion promoting agent, diluent, deionized water, mass fraction of each component is 60 cement 70, 25, 14 masterbatch reactive acrylic resin, epoxy resin 5 9 8 9 2, 3.6, pigment adhesion promoter 2.2 4.6, 8, 6 diluent deionized water 60 80. Concrete is a porous substance, and capillary and micro cracks are the fundamental causes of leakage. If the pore passage and micro cracks are blocked, it will be able to resist weathering, while cement based permeable crystalline waterproof coating is the use of this principle to achieve the purpose of weathering. The waterproof coating has the advantages of simple production process, convenient construction, anti weathering, waterproof and impermeability.
【技术实现步骤摘要】
一种防渗水涂料
本专利技术涉及一种涂料制备
，具体地讲，本专利技术涉及一种防渗水涂料。
技术介绍
乳胶漆即是乳液性涂料，按照基材的不同，分为聚醋酸乙烯乳液和丙烯酸乳液两大类。乳胶漆以纤维素为稀释剂，是一种施工方便、安全、耐纤维素洗、透气性好的的涂料，它可根据不同的配色方案调配出不同的色泽。种类：水性内墙漆、油性内墙漆、干粉型内墙漆，属纤维素性涂料，主要由水，乳液，颜料，填料，添加剂五种成分构成。涂料是涂覆在被涂的物件的表面，并能形成牢固附着的连续薄膜的材料。涂料广泛用于化工设备、贮槽、管道、容器的耐腐蚀涂料，涂覆食品接触盖表面的涂料，家电、电子元件和工业设备的功能性涂料。但现有的涂料，存在着高温时耐溶剂性差、粘结性能差、涂料外观美感差，主要用于保护涂层而不用于装饰性涂层等问题。
技术实现思路
针对现有技术中存在的上述不足，本专利技术所要解决的技术问题是提供一种效果好的防渗水涂料。本专利技术解决其技术问题所采用的技术方案是：提供一种防渗水涂料，其特征在于：包括水泥、活性母料、丙烯酸树脂、环氧树脂、颜填料、附着力增进剂、稀释剂、无离子水，各组分的质量份数为：水泥60...
【技术保护点】
一种防渗水涂料，其特征在于：包括水泥、活性母料、丙烯酸树脂、环氧树脂、颜填料、附着力增进剂、稀释剂、无离子水，各组分的质量份数为：水泥60‑70、活性母料14‑25、丙烯酸树脂5‑9、环氧树脂8‑9、颜填料2‑3.6、附着力增进剂2.2‑4.6、稀释剂6‑8、无离子水60‑80。
【技术特征摘要】
1.一种防渗水涂料，其特征在于：包括水泥、活性母料、丙烯酸树脂、环氧树脂、颜填料、附着力增进剂、稀释剂、无离子水，各组分的质量份数为：水泥60-70、活性母料14-25、丙烯酸树脂5-9、环氧树脂8-9、颜填料2-3.6、附着力增进剂2.2-4.6、稀释剂6-8、无离子水60-80。2.根据权利要求1所述的防渗水涂料，其特征在于：所述防渗水涂料各组分的质量份数为：水泥60、活性母料14、丙烯酸树脂5、环氧树脂8、颜填料2、附着力增进剂2.2、稀释剂6...