一种高荧光氮掺杂碳量子点、其制备方法及应用技术

本发明专利技术公开了一种高荧光氮掺杂碳量子点、其制备方法及应用。将L‑瓜氨酸溶解于去离子水中使其浓度为0.010～0.040 g/mL，超声震荡5～20 min，再采用水热法在180～220℃反应8～24 h获取碳点溶液；将碳点溶液在17000～20000 r/min超速离心20～40 min，再用0.22μm滤膜过滤，获得碳点溶液。高荧光氮掺杂碳量子点在豆芽和宫颈癌细胞中的应用。本发明专利技术的荧光效率高，制备简单，低毒、良好的生物相容性及水溶性、粒径小。

High fluorescent nitrogen doped carbon quantum dot, preparation method and application thereof

The invention discloses a high fluorescent nitrogen doped carbon quantum dot, a preparation method and an application thereof. L citrulline dissolved in deionized water, the concentration of 0.010 to 0.040 g/mL, 5 ~ 20 min sonication, then by hydrothermal method at 180 to 220 DEG C 8 ~ 24 h access point carbon solution; the carbon solution in 17000 ~ 20000 and 20 ~ 40 r/min ultracentrifugation min then, 0.22 M filter membrane filtration, carbon solution. Application of high fluorescent nitrogen doped carbon quantum dots in bean sprouts and cervical cancer cells. The invention has the advantages of high fluorescence efficiency, simple preparation, low toxicity, good biocompatibility, water solubility and small particle size.

【技术实现步骤摘要】
一种高荧光氮掺杂碳量子点、其制备方法及应用
本专利技术属于碳纳米材料领域，具体涉及一种高荧光氮掺杂碳量子点，同时还涉及该高荧光氮掺杂碳量子点的制备方法，及该高荧光氮掺杂碳量子点在生物成像中的应用。
技术介绍
重金属量子点因其出色的发光性能被广泛的研究，然而，他们大部分具有较高的毒性和较高的生产成本。探究生物相容性好、优良光致发光性能、低毒，较小粒径的荧光材料，并满足生物成像、药物运输、荧光油墨等应用，具有较大潜在应用价值。荧光碳量子点由生物相容性优异的碳元素作为核心组件，量子点材料因其纳米大小又常表现出宏观尺寸材料所不具备的特异性能，并具有良好的光学性能，高亮度和小尺寸是碳量子点最具吸引力的两个优点，因而吸引了科学家极大的关注。因碳量子点的平均尺寸小于10nm，易进入细胞或动物体后仍保持荧光性能，可用为荧光探针跟踪生物大分子或生物反应过程。因此，荧光碳量子点具有广泛的应用前景，包括生物传感、成像、光催化、药物运输和荧光油墨等领域。目前，研究者建立了多种制备荧光碳量子点的方法：激光刻蚀法、电弧放电法、化学氧化法、电化学法、超声处理、微波辐射法和水热法。其中，水热法被认为是一种简单、高效本文档来自技高网...

【技术保护点】
一种高荧光氮掺杂碳量子点，其氮的含量可达15.5～19.2%，平均荧光寿命为4.41～4.51 ns，荧光量子产率在20.3～32.9%。

【技术特征摘要】
1.一种高荧光氮掺杂碳量子点，其氮的含量可达15.5～19.2%，平均荧光寿命为4.41～4.51ns，荧光量子产率在20.3～32.9%。2.一种高荧光氮掺杂碳量子点的制备方法，包括以下步骤：（1）将L-瓜氨酸溶解于去离子水中使其浓度为0.010-0.040g...

【专利技术属性】
技术研发人员：张仟春，谢思琪，王兴益，付予锦，李飞，王苑，
申请(专利权)人：兴义民族师范学院，
类型：发明
国别省市：贵州,52